介绍了纳米陶瓷微粒的液相沉积表面包覆改性方法,包括沉淀法、非均匀形核法、超声化学法、溶胶-凝胶法、非均相凝聚法、化学镀法,指出了这些改性方法的优缺点及关键工艺条件,并综述了液相沉积法表面包覆改性的机理.
参考文献
| [1] | 高濂;孙静;刘阳桥.纳米粉体的分散及表面改性[M].北京:化学工业出版社,2003:207. |
| [2] | 张立德;牟季美.纳米材料和纳米结构[M].北京:科学出版社,2001:140. |
| [3] | 孙尧,周刚.纳米陶瓷及其应用前景[J].化工新型材料,2001(07):6-8. |
| [4] | 宿辉,邹桂真,曹茂盛.SiC纳米/微米粒子表面修饰、涂覆的研究进展[J].材料工程,2004(10):57-60. |
| [5] | Wang J;Gao L .Adsorption of polyethylenimine on nanosized zirconia particles in aqueous suspensions[J].Journal of Colloid and Interface Science,1999,21(06):436. |
| [6] | Yang J.;Weng WJ.;Ferreira JMF. .Dispersion properties of silicon nitride powder coated with yttrium and aluminium precursors[J].Journal of Colloid and Interface Science,1998(1):274-280. |
| [7] | Zhang Rui;Gao Lian;Guo Jingkun.Preparation and characterization of coated nanoscale Cu/SiCp composite particles[J].CERAMICS INTERNATIONAL,2004(30):401. |
| [8] | Zhang R.;Gao L.;Guo JK. .Temperature-sensitivity of coating copper on sub-micron silicon carbide particles by electroless deposition in a rotation flask[J].Surface & Coatings Technology,2003(1):67-71. |
| [9] | 张锐,高濂,虞玲,郭景坤.粒度分布对Cu包覆SiC颗粒相分布均匀性的影响[J].无机材料学报,2002(06):1311-1314. |
| [10] | 陈志刚,陈彩凤,刘苏.超声场中湿法制备A12O3纳米粉工艺研究[J].硅酸盐学报,2003(02):213-217. |
| [11] | 姚超,吴凤芹,林西平,杨绪杰,陆路德,汪信.超声场中纳米TiO2表面包覆氧化硅的研究[J].无机化学学报,2005(01):59-64. |
| [12] | 孙秀果,魏雨,贾振斌,马子川.纳米TiO2包硅处理及其性能的研究[J].半导体技术,2003(01):69-71. |
| [13] | 邹建,高家诚,王勇,李易东,文敏.纳米TiO2表面包覆致密SiO2膜的试验研究[J].材料科学与工程学报,2004(01):71-73. |
| [14] | 崔爱莉,王亭杰,金涌,孙牧.二氧化钛表面包覆氧化硅纳米膜的热力学研究[J].高等学校化学学报,2001(09):1543-1545. |
| [15] | [OL].http://www.multiphase.newcastle.edu.au/papers/1998/penpolcharoen.pdf |
| [16] | Hongzhi Wang;Hiroyuki Nakamura;Ken Yao .Effect of Polyelectrolyte Dispersants on the Preparation of Silica-Coated Zinc Oxide Particles in Aqueous Media[J].Journal of the American Ceramic Society,2002(8):1937-1940. |
| [17] | 田彦文.化学镀法制备Ni包覆ZrO2微粉[J].腐蚀科学与防护技术,1998(06):355. |
| [18] | 范启义,凌国平,郦剑.化学镀铜法制备纳米Cu-Al2O3复合粉体的研究[J].材料科学与工艺,2002(04):357-361. |
| [19] | 邹建,高家诚,王勇,李易东,文敏.纳米TiO2表面包覆氧化铝的热力学[J].功能材料,2004(05):573-575. |
| [20] | 覃操,王亭杰,金涌.液相沉积法制备TiO2颗粒表面包覆SiO2纳米膜[J].物理化学学报,2002(10):884-889. |
| [21] | 孙秀果,贾振斌,魏雨.纳米级二氧化钛包硅过程及形成机理研究[J].河北师范大学学报(自然科学版),2002(06):598-601. |
| [22] | 孔德玉,王家邦,韦苏,程本军,杨辉.纳米SiO2包覆Al2O3浓悬浮体制备及其凝胶注模成型[J].硅酸盐学报,2004(04):442-447. |
| [23] | 崔爱莉,王亭杰,金涌.SiO2和Al2O3在TiO2表面的成核包覆与成膜包覆[J].化工冶金,1999(02):178-181. |
| [24] | 章永化,陈守明,陈建华,熊红兵,张启卫,沈辉,龚克成.纳米Fe3O4/聚苯乙烯均匀分散体系的制备及结构[J].高等学校化学学报,2003(09):1717-1720. |
| [25] | Zhou Yu .Surface polymerization,interface structure,and low temperature consolidation of nano ceramic particles[D].Department of Material Science and Engineering of the College of Engineering of the Univisity of Cincinnati,2000. |
| [26] | Jean JH.;Wang HR. .Dispersion of aqueous barium titanate suspensions with ammonium salt of poly(methacrylic acid)[J].Journal of the American Ceramic Society,1998(6):1589-1599. |
| [27] | 郭兴忠,杨辉,曹明,王建武.聚乙烯亚胺表面改性SiC粉体的流动特性[J].化工学报,2004(05):800-804. |
| [28] | 王瑞刚,吴厚政,陈玉如,杨正方.陶瓷料浆稳定分散进展[J].陶瓷学报,1999(01):35-40. |
| [29] | 崔爱莉,陈仁政,尉京志,李龙土.超细钛酸钡的表面改性[J].高等学校化学学报,2001(12):2065-2067. |
| [30] | 覃超;王亭杰;金涌.TiO2颗粒表面包覆Al2O3纳米膜的特性[J].过程工程学报,2002(11):87. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%