研究了百菌清作为抗菌剂对麦秸秆/PP复合材料耐腐蚀性能的影响,制备5种百菌清含量的麦秸秆/PP复合材料,参照ASTMG21-96对复合材料进行腐蚀实验,并测试腐蚀后麦秸秆/PP复合材料的力学性能、吸水性能、色差以及表面微观结构.结果表明:百菌清添加量为1.25％时,腐蚀后麦秸秆/PP复合材料的综合性能较好,与不添加抗菌剂的复合材料相比,弯曲强度、弯曲弹性模量、拉伸强度、冲击强度分别提高了13.71％,54.91％,10.46％,47.53％,吸水192h的吸水率降低了23.69％,腐蚀前后色差值则减小了11.56.
参考文献
| [1] | 雷彩红,雷芳,陈福林.户外木塑复合材料的研究进展[J].塑料,2007(01):22-26,61. |
| [2] | Klyosov A.A.Wood-Plastic Composites[M].北京:科学出版社,2010:324. |
| [3] | Wood-plastic composites: current trends in materials and processing[J].Plastics, additives & compounding,2005(5):20,22-26-0. |
| [4] | MORRIS P I;COOPER P .Recycled plastic/wood composite lumber attacked by fungi[J].Forest Products Journal,1998,48(01):86-88. |
| [5] | VERHEY S;LAKS P .Wood particle size affects the decay resistance of wood fiber/thermoplastic composites[J].Forest Products Journal,2002,52(11/12):78-81. |
| [6] | John Simonsen;Camille M. Freitag;Antonio Silva;Jeffrey J. Morrell .Wood/plastic ratio: Effect on performance of borate biocides against a brown rot fungus[J].Holzforschung,2004(2):205-208. |
| [7] | LAKS P;VEHRING K;VERHEY S.Effect of manufacturing variables on mold susceptibility of wood-plastic composites[A].Madison:USDA Forest Products Laboratory,2005:265-270. |
| [8] | IBACH R E;SCHUMANN R L;CLEMONS C M.Wood-plastic composites with reduced moisture:effects of chemical modification on durability in the laboratory and field[A].Madison:USDA Forest Products Laboratory,2007:259-266. |
| [9] | Pendleton DE;Hoffard TA;Adcock T;Woodward B;Wolcott MP .Durability of an extruded HDPE/wood composite[J].Forest Products Journal,2002(6):21-27. |
| [10] | 蒋明亮 .新型木材防腐剂-百菌清的研究近况[J].木材工业,1997,11(04):21-22. |
| [11] | 蒋明亮 .百菌清制剂防霉效果的初步研究[J].工业木材,1998,12(02):22-23. |
| [12] | 蒋明亮.低毒防腐剂百菌清及铜制剂对木材尺寸稳定及力学性能的影响*[J].林业科学,2001(04):107-110. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%