本文通过使用机械方法制备了不同种类的泡沫混凝土，并研究了不同容重（300～1200 kg／m3）、水胶比（0．3～0．6）、聚丙纤维、EPS颗粒对其力学性能的影响。采用了SEM分析了各配比的微观结构，进而解释其强度的变化。结果表明，容重是影响泡沫混凝土宏观及微观性能最重要的因素，通过容重的控制可以得到满足不同需要的产品，容重越大强度越高。此外，聚丙纤维的掺入在一定范围内可以增加强度；EPS颗粒的掺入可以降低容重，但也会带来强度的下降。
The influence of the different densities (300-1200 kg/m3), water-binder ratio (0.3-0.6), the polypropylene fiber and the EPS particles were investigated .The microstructure of a variety of proportions was analyzed by SEM and then explain the change of the strength .The result shows that the density is the most important factors of foam concrete macroscopic and microscopic property .Through the density control ,the different needs of products can be obtained .The higher the density is ,the greater the strength will be.In addition, the polypropylene fiber mixed can increase the strength in a certain range .The addition of EPS particles can lower bulk density , but also can make strength decline .
参考文献
| [1] | 陆宁;林冠宏;俞允凯;马红军;王源青.2003～2007年中国城镇建筑能耗的分类分析[J].建筑经济,2009(12):95-97. |
| [2] | 苑静.建筑节能保温材料的发展及前景[J].消费导刊,2010(02):207. |
| [3] | 张红;曹亚楠.浅谈建筑能耗的现状和节能的重要性[J].林业科技情报,2005(2):31. |
| [4] | 王天民;王莹.低碳经济及其对新材料研究开发的挑战[J].中国材料进展,2010(1):60-64. |
| [5] | 闫振甲.泡沫混凝土有望成为保温材料首选[J].混凝土世界,2010(01):22-26. |
| [6] | 林兴胜 .纤维增强泡沫混凝土的研制与性能[D].合肥工业大学,2007. |
| [7] | 陈惠霞.泡沫混凝土强度的影响因素及质量控制[J].山西建筑,2009(32):163-164. |
| [8] | 蔡娜 .超轻泡沫混凝土保温材料的试验研究[D].重庆大学,2009. |
| [9] | 张佚伦 .聚丙烯纤维混凝土早期收缩与抗裂性能试验研究[D].浙江大学,2006. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%