The synthesis,crystal structure and electrical conductivity properties of Fe-doped ZnO powders（in the range of 0.25-15 mol%） were reported in this paper.I-phase samples,which were indexed as single phase with a hexagonal（wurtzite） structure in the Fe-doped ZnO binary system,were determined by X-ray diffraction（XRD）.The solubility limit of Fe in the ZnO lattice is 3 mol% at 950℃.The above mixed phase was observed.And the impurity phase was determined as the cubic-ZnFe 2 O 4 phase when compared with standard XRD data using the PDF program.This study focused on single I-phase ZnO samples which were synthesized at 950℃ because the limit of the solubility range is the widest at this temperature.The lattice parameters a and c of the I-phase decreased with Fe-doping concentration.The morphology of the I-phase samples was analyzed with a scanning electron microscope.The grain size of the I-phase samples increased with heat treatment and doping concentration.The electrical conductivity of the pure ZnO and single I-phase samples was investigated using the four-probe dc method at 100-950℃ in air atmosphere.The electrical conductivity values of pure ZnO,0.25 and 3 mol% Fe-doped ZnO samples at 100℃ were 2×10-6,1.7×10-3 and 6.3×10-4 S.cm-1,and at 950℃ they were 3.4,8.5 and 4 S.cm-1,respectively.
参考文献
| [1] | D. W. Zeng;C. S. Xie;B. L. Zhu .Synthesis and characteristics of Sb-doped ZnO nanoparticles[J].Materials Science & Engineering, B. Solid-State Materials for Advanced Technology,2003(1/2):68-72. |
| [2] | K. Park;K.Y. Ko .Effect of TiO_2 on high-temperature thermoelectric properties of ZnO[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2007(1/2):200-204. |
| [3] | M.L. Dinesha;H.S. Jayanna;S. Ashoka .Temperature dependent electrical conductivity of Fe doped ZnO nanopartides prepared by solution combustion method[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2009(1/2):538-541. |
| [4] | Y. Natsume;H. Sakata .Zinc oxide films prepared by sol-gel spin-coating[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2000(1/2):30-36. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%