采用传统陶瓷制备方法制备了致密的NaNbO3无铅铁电陶瓷。利用XRD、SEM、介电温谱等分析技术,研究了CuO和MnO2掺杂对NaNbO3无铅铁电陶瓷的合成温度、烧成工艺、结构相变以及铁电性能的影响。结果表明通过CuO和MnO2掺杂能在较低温度下制备出致密的NaNbO3陶瓷和陶瓷的致密度,电学性能随着烧成温度的变化存在一个最优值,最佳烧结温度为1050℃,体积密度达到4.38g/cm3为理论密度的98.6%。该陶瓷在15～120℃均表现出铁电性能,具有压电活性,常温下介电常数为287,居里温度为390℃。
In this paper,NaNbO3 lead-free ferroelectric ceramics was synthesized by a conventional solid state reaction at a low temperature.The effect of CuO and MnO2 on sintering temperature,structure and properties was studied by XRD,SEM and other methods.The result shows that CuO and MnO2-doped dense NaNbO3 lead-free ceramics was obtained at a low sintering temperature.The properties of NaNbO3 ceramics had a best sintering temperature of 1050℃.The density was 4.38g/cm3 and reached 98.6% of the theoretical density.Ferroelectric properties were observed from 15-120℃,the Curie temperature was 390℃.The dielectric constant was 287 and the dielectric loss was less than 2% at room temperature.
参考文献
| [1] | 赁敦敏,肖定全,朱建国,余萍,鄢洪建.铌酸盐系无铅压电陶瓷的研究与进展--无铅压电陶瓷20年专利分析之四[J].功能材料,2003(06):615-618. |
| [2] | 明保全,王矜奉,臧国忠,王春明,盖志刚,杜鹃,郑立梅.铌酸钾钠基无铅压电陶瓷的X射线衍射与相变分析[J].物理学报,2008(09):5962-5967. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%