用电化学法和表面形貌观察研究AZ91D镁合金电镀铜前酸洗活化及浸锌过程的一些主要影响因素．结果表明，镁合金的酸洗活化液组成对镁合金表面的光洁度有较大影响，复合组分（C2H2O4·2H2O＋NaF）酸洗活化效果明显好于单一组分（C2H2O4·2H2O）的酸洗活化液，酸洗活化的温度以常温为宜．最佳酸洗活化工艺为：12g／LC2H2O4·2H2O，50g／LNaF，温度25-35℃，时间60-300S．浸锌液中的NaF和Na2COa对镁合金浸锌效果有重要影响，二者缺一不可；变温浸锌获得的浸锌层效果优于恒温浸锌，最佳浸锌温度为是30℃变温到40℃：浸锌时间以10min到15min为宜．
To deeply understand pretreatment process of AZ91D magnesium alloy for copper electroplating, the major factors which influence the pickling-activation and zincifying of magnesium alloy AZ91D were investigated by electrochemical measurement and scanning electron microscopy （SEM）. The results show that the composition of pickling-activation bath has considerable influence on the surface roughness of AZ91D magnesium alloy. The pickling-activation effectiveness of a compound （C2H2O4.2H2O＋NaF） bath is better than that of single （C2H2O4.2H2O） bath. The appropriate temperature of pickling-activation is room temperature. The optimal formula of picking-activation is 12 g/L C2H2O4.2H2O, 50 g/L NaF, T=25 35 ℃, t=60-300 s. The pres- ence of both NaF and Na2CO3 could have considerable influence on the open circuit potential （OCP） and the surface morphology of magnesium alloy AZ91D for zincifying. The zincifying film obtained in a zincifying bath with continuously varied temperatures was better than that with a consistent temperature. The optimal temperature regime varied continuously from 30℃ to 40 ℃. The appropriate immersion time of zincifying is 10-15 min.
参考文献
| [1] | Huang C A, Wang T H, Weirich T, et al. A pretreat- ment with galvanostatic etching for copper electrodeposi- tion on pure magnesium and magnesium alloys in an alka- line copper-sulfate bath[J]. Electrochim. Acta , 2008, 53 (24): 7235. |
| [2] | 孙忠武,钱建刚,黄巍等.镁合金浸锌合金溶液中金属离子对浸锌层的影响[J].材料保护,2009,42(1):27. |
| [3] | Sharma A K, Suresh M R, Bhojraj H, et al. Electro- less nickel plating on magnesium alloy[J]. Met. Finish., 1998, 96 (3): 10. |
| [4] | 孙硕,刘建国,张伟等.镁合金无铬无氟前处理直接化学镀镍研究[J].腐蚀科学与防护技术,2009,21(3):277. |
| [5] | Fairweather W A . Electroless nickel plating of magne- sium[J]. Trans. Inst. Met Finish., 1997, 75(3): 113. |
| [6] | Lawrie B. UK company leads the way in magnesium plat- ing [J]. Finishing, 1994, 18(11): 22. |
| [7] | Gray J E, Luan B. Protective coating on magnesium and its alloys-a critical review[J]. J. Alloys Compd., 2002, 336: 88. |
| [8] | Kato J, Urushihara W, Nakayama T. Magnesium based al- loys artical and a method thereof [P]. USP: 6068938, 2000. |
| [9] | 余刚,刘云娥,胡波年等.镁合金焦磷酸盐镀铜工艺的研究[J].湖南大学学报(自然科学版),2005,32(4):77. |
| [10] | 卢神保,曾冬铭,张其林.AZ91D镁合金电镀前处理酸洗工艺的研究[J].电镀与环保,2009,29(4):10. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%