利用热分析技术对具有高温快速固化性能的间苯二酚缩水甘油醚/间苯二甲胺体系的热机械性能和表观固化反应动力学进行了研究。热机械性能分析（DMA和TMA）结果表明,间苯二酚缩水甘油醚/间苯二甲胺固化产物的玻璃化转变温度为83℃,室温下储能模量为2600 MPa,玻璃态热膨胀系数（α1）为54.9×10-6℃-1,橡胶态的线性热膨胀系数（α2）为177.9×10-6℃-1。通过恒温和非恒温模式差示扫描量热（DSC）测试得到体系的表观反应活化能为62.7 kJ/mol,由此估算出固化反应在160℃时仅需数秒即可完成。
The thermal and mechanical properties of a fast curing system,resorcinol diglycidyl ether/m-xylylene diamine（RDGE/XDA）,were investigated by means of thermal analysis techniques.The results of dynamic mechanical analysis（DMA） and thermo-mechanical analysis（TMA） show that the glass transition temperature of RDGE/XDA is 83 ℃,and the storage modulus at room temperature is 2600 MPa.The coefficients of thermal expansion corresponding to the glassy and rubbery state is 54.9×10-6 ℃-1 and 177.9×10-6 ℃-1,respectively.The apparent activation energy obtained through isothermal and non-isothermal differential scanning calorimetry（DSC） measurement is 62.7 kJ/mol.Thus,the curing process of RDGE/XDA takes only a few seconds at 160 ℃ estimated from the curing rate at lower temperature and the apparent activation energy.
参考文献
| [1] | Vinnik RM;Roznyatovsky VA .Kinetic method by using calorimetry to mechanism of epoxy-amine cure reaction - Part VII. Resorcinol diglycidylether-aniline[J].Journal of thermal analysis and calorimetry,2006(1):193-198. |
| [2] | 宁保江.高性能、低成本复合材料用环氧体系的研究[J].热固性树脂,2009(02):29-31,38. |
| [3] | Zhu, M.;Li, Y.;Zhang, Q.;Wang, H. .Mechanical properties of dental resin composites by co-filling diatomite and nanosized silica particles[J].Materials science & engineering, C. Biomimetic and supramolecular systems,2011(3):600-605. |
| [4] | He Y. .DSC and DEA studies of underfill curing kinetics[J].Thermochimica Acta: An International Journal Concerned with the Broader Aspects of Thermochemistry and Its Applications to Chemical Problems,2001(0):101-106. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%