结合高能球磨和放电等离子烧结制备出具有粗晶组织、粗细晶双尺度组织和超细晶组织的TC4合金;采用球-盘微动磨损装置对比研究了这3种显微组织TC4合金在干摩擦条件下的微动磨损性能,分析了晶粒细化对TC4合金摩擦磨损性能的影响.结果表明:随着晶粒的逐步细化,TC4合金的摩擦系数和磨损率逐渐降低.这主要是因为晶粒细化导致TC4合金硬度逐渐提高,并引起磨损机制的转变.粗晶TC4合金的磨损机制为严重的粘着磨损、疲劳剥层磨损和氧化磨损;而双尺度和超细晶TC4合金的磨损机制以磨粒磨损为主并伴随着轻微的粘着磨损和氧化磨损.超细晶TC4合金拥有最高的硬度(HV为4560 MPa),在载荷30N下具有最低的摩擦系数(～0.76)和磨损率(1.89× 10-4 mm3·N1·ml),说明晶粒细化有助于提高TC4合金的摩擦磨损性能.
参考文献
| [1] | Sergueeva AV.;Stolyarov VV.;Valiev RZ.;Mukherjee AK. .Superplastic behaviour of ultrafine-grained Ti-6A1-4V alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2002(1/2):318-325. |
| [2] | Gao, N.;Wang, C.T.;Wood, R.J.K.;Langdon, T.G. .Tribological properties of ultrafine-grained materials processed by severe plastic deformation[J].Journal of Materials Science,2012(12):4779-4797. |
| [3] | Amanov, A.;Cho, I.-S.;Kim, D.-E.;Pyun, Y.-S..Fretting wear and friction reduction of CP titanium and Ti-6Al-4V alloy by ultrasonic nanocrystalline surface modification[J].Surface & Coatings Technology,2012:135-142. |
| [4] | 孟庆武,耿林,王春华,刘树林,韩文静.两种热处理钛合金的摩擦磨损性能[J].大庆石油学院学报,2006(04):46-48. |
| [5] | 卫中山,王珉,张明,丁文江.TC4钛合金的微动疲劳行为研究[J].稀有金属材料与工程,2006(07):1050-1052. |
| [6] | 侯滨,黄伟九,陈波水,周仲荣,李春生.AZ91D镁合金滑移区域微动磨损机理研究[J].摩擦学学报,2004(04):351-354. |
| [7] | 王镇波,雍兴平,陶乃殚,李曙,刘刚,吕坚,卢柯.表面纳米化对低碳钢摩擦磨损性能的影响[J].金属学报,2001(12):1251-1255. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%