Effects of Forging and Heat Treatments on the Microstructure and Oxidation Behavior of 316LN Stainless Steel in High Temperature Water

材料科学技术（英文）, 2015, 31(4): 403-412.

Yueling Guo ^1, , En-Hou Han ^2, , Jianqiu Wang ^3,

1.National Center for Materials Service Safety, University of Science and Technology Beijing, Beijing 100083, China

2.National Center for Materials Service Safety, University of Science and Technology Beijing, Beijing 100083, China ; Key Laboratory of Nuclear Materials and Safety Assessment, Institute of Metal Research, Chinese Academy of Science, Shenyang 110016, China

3.Key Laboratory of Nuclear Materials and Safety Assessment, Institute of Metal Research, Chinese Academy of Science, Shenyang 110016, China

基金项目: This work was supported by the National Science and Technology Major Project (No.2011ZX06004-009).

Effects of Forging and Heat Treatments on the Microstructure and Oxidation Behavior of 316LN Stainless Steel in High Temperature Water

Keywords： Stainless steel

参考文献

[1]	J. Hou;Q.J. Peng;T. Shoji;J.Q. Wang;E-H. Han;W. Ke .Effects of cold working path on strain concentration, grain boundary microstructure and stress corrosion cracking in Alloy 600[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2011(9):2956-2962.
[2]	J. Hou;Q.J. Peng;Z.P. Lu;T. Shoji;J.Q. Wang;E.-H. Han;W. Ke .Effects of cold working degrees on grain boundary characters and strain concentration at grain boundaries in Alloy 600[J].Corrosion Science,2011(3):1137-1142.
[3]	V.Y. GERTSMAN;S. M. BRUEMMER .STUDY OF GRAIN BOUNDARY CHARACTER ALONG INTERGRANULAR STRESS CORROSION CRACK PATHS IN AUSTENITIC ALLOYS[J].Acta materialia,2001(9):1589-1598.
[4]	N. K. Das;T. Shoji .Early Stage Oxidation Initiation at Different Grain Boundaries of fcc Fe-Cr Binary Alloy: A Computational Chemistry Study[J].Oxidation of Metals,2013(3/4):429-441.
[5]	M.P. Phaniraj;Dong-Ik Kim;Young Whan Cho .Effect of grain boundary characteristics on the oxidation behavior of ferritic stainless steel[J].Corrosion Science,2011(12):4124-4130.
[6]	G. Palumbo;K. T. Aust;E. M. Lehockey;U. Erb;P. Lin .On a more restrictive geometric criterion for "special" CSL grain boundaries[J].Scripta materialia,1998(11):1685-1690.
[7]	S. CARLSSON;P. -L. LARSSON .ON THE DETERMINATION OF RESIDUAL STRESS AND STRAIN FIELDS BY SHARP INDENTATION TESTING[J].Acta materialia,2001(12):2179-2191.
[8]	F. Huang,J.Q. Wang,E.H. Han,W. Ke.Short-time Oxidation of Alloy 690 in High-temperature and High-pressure Steam and Water[J].材料科学技术学报：英文版,2012(06):562-568.
[9]	T. SUNDARARAJAN;S. KURODA;K. NISHIDA .Behaviour of Mn and Si in the Spray Powders during Steam Oxidation of Ni-Cr Thermal Spray Coatings[J].ISIJ International,2004(1):139-144.
[10]	S. Lozano-Perez;T. Yamada;T. Terachi .Multi-scale characterization of stress corrosion cracking of cold-worked stainless steels and the influence of Cr content[J].Acta materialia,2009(18):5361-5381.
[11]	S.G. Wang;M. Sun;H.B. Han;K. Long;Z.D. Zhang .The high-temperature oxidation of bulk nanocrystalline 304 stainless steel in air[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2013(Jul.):64-72.

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
Yueling Guo En-Hou Han Jianqiu Wang
在百度学术搜索
Yueling Guo En-Hou Han Jianqiu Wang
在万方数据库搜索
Yueling Guo En-Hou Han Jianqiu Wang
在CNKI搜索
Yueling Guo En-Hou Han Jianqiu Wang

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

Effects of Forging and Heat Treatments on the Microstructure and Oxidation Behavior of 316LN Stainless Steel in High Temperature Water

参考文献