含铝钢连铸时,钢水中的铝与保护渣中SiO2反应导致保护渣中Al2O3含量增加而SiO2含量减少,导致保护渣的热物理性能发生变化,从而影响了铸坯的质量。在以前的研究基础上使用X射线衍射仪（XRD）和差热分析仪（DTA）以及扫描电镜（SEM）研究了高铝保护渣固态渣膜的结晶行为与晶体显微结构的变化规律。结果表明,高铝保护渣中CaF2的析出主要是因为SiO2含量的减少和Al2O3含量的增加导致大量的Ca2＋的功能由电荷补偿变为网络修饰体,温度降低时CaF2首先析出;随着保护渣中Al2O3含量的增加,在同一加热速率下析晶温度升高;当保护渣中Al2O3含量较少时,析出晶体为枪晶石（Ca4Si2O7F2）和少量的CaF2,当Al2O3含量大于5%（质量分数,下同）时,霞石（NaAlSiO4）进一步析出,且随着Al2O3含量的增加,析出晶体的尺寸减小。
The content of SiO2 deceases while Al2O3 increases in the mold flux on the casting of the steel containing high aluminium,which will cause the thermo-physical properties of the mold flux change,then influence the quality of the casting blank.On the base of the previous investigation,the crystallization behavior and the microstructure change with varying compositions of solid mold slag used in casting steels containing high Al was investigated through using differential thermal analysis（DTA） and X-ray diffraction technique（XRD）,and the scanning electron microscope（SEM） techniques.The results indicate that the precipitation mechanism of CaF2 is because that the role of Ca2＋ transforms from network charge compensation to networker modifiers with Al2O3 content increasing and the SiO2 decreasing,resulting in the precipitation of CaF2 firstly as the temperature decreases;the temperature of the crystallization is increasing at the same heating rate while the Al2O3 increasing;and the precipitated crystals transiting from single cuspidine phase contain a little CaF2 to nepheline appear and increase as the alumina content exceeds 5%,the size of the crystals is decreasing with the increasing of the alumina content.
参考文献
| [1] | Takehide SENUMA .Physical Metallurgy of Modern High Strength Steel Sheets[J].ISIJ International,2001(6):520-532. |
| [2] | Inclusion Characterization and Thermodynamics for High-Al Advanced High-strength Steels[J].Iron & Steel Technology,2006(6):64-73. |
| [3] | WANLIN WANG;KENNETH BLAZEK;ALAN CRAMB .A Study of the Crystallization Behavior of a New Mold Flux Used in the Casting of Transformation-Induced-Plasticity Steels[J].Metallurgical and Materials Transactions, B. Process metallurgy and materials processing science,2008(1):66-74. |
| [4] | YU X;WEN G H;TANG P et al.Behaviror of Mold Slag Used for 20Mn23AI Nonmagnetic Steel During Casting[J].Journal of Iron and Steel Research International,2011,18(01):20. |
| [5] | Ryu H G;ZHANG Z T;Cho J W .Crystallization Behavior of Slag Through a Heat Flux Simulator[J].ISIJ International,2010,50(08):1142. |
| [6] | Watanabe T;Fukuyama H;Nagata K et al.Stability of Cus- pidine and Phase Relations in the CaO-SiO2-CaF2 System[J].ISIJ International,2002,42(05):489. |
| [7] | ZHANG Z T;WEN G H;TANG P et al.The Influence of AlzO3/SiO2 Ratio on the Viscosity of Mold Fluxes[J].ISIJ International,2008,48(06):739. |
| [8] | ZHANG Z T;WEN G H;LIAO J L et al.Effect of AtzO3/ SiO2 Ratio on the Crystallization Behavior of Mold Slag[J].Steel Research International,2010,81:551. |
| [9] | Loewenstein W .The Distribution of Aluminium in the Tetra- hedra of Silicates and Aluminates[J].American Mineralogist,1954,39:92. |
| [10] | Erkmen Z E;Catakli E;Ovecoglu L M .Characterisation and Crystallisation Kinetics of Glass Ceramics Developed From Erdemir Blast Furnace Slags Containing Cr2 03 and TiO2 Nu- cleant[J].Advance in Applied Ceramics,2009,108(01):57. |
| [11] | Matusita K;Sakka S .Kinetic Study of Crystallization of Glass by Differential Thermal Analysis-Criterion on Applica- tion of Kissinger Plot[J].Journal of Non-Crystalline Solids,1980,38/39(02):741. |
| [12] | Kissinger H E .Variation of Peak Temperature With Heating Rate in Differential Thermal Analysis[J].Journal of Re- search of the National Bureau of Standards,1956,57(04):217. |
| [13] | Kissinger H E .Reaction Kinetics in Differential Thermal Analysis[J].Analytical Chemistry,1957,29(11):1702. |
| [14] | Ray C S;Quanyu Y;Weihai H .Surface and Internal Crystal- lization in Glasses as Determined by Differential Thermal Analysis[J].Journal of the American Ceramic Society,1996,79(12):3155. |
| [15] | Ozawa T .Kinetics of Non-Isothermal Crystallization[J].Polymer,1971,12(03):150. |
| [16] | 赵艳红,唐萍,文光华,巴钧涛,漆鑫.保护渣碱度对渣膜传热的影响[J].过程工程学报,2008(z1):205-209. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%