为了研究合金元素对块体纳米晶Fe3Al材料磁学性能的影响,通过铝热反应熔化法制备了纳米晶Fe3Al以及分别含Ni质量分数10%、Cr质量分数10%、Mn质量分数10%和含Ni质量分数10%-Cu质量分数2%的块体纳米晶Fe3Al.在振动样品磁强计（VSM）上测得合金的磁滞回线,分析其磁性能,采用X射线衍射仪进行结构分析和平均晶粒尺寸计算.结果表明：各样品的磁滞回线呈倾斜状且狭长,磁滞损耗很小;含Ni质量分数10%的样品饱和磁化强度Ms较大,剩余磁化强度Mr和矫顽力Hc较其他样品最小,具有较好的软磁性能;添加合金元素后几种材料的晶粒尺寸变小,磁性能有较大变化,合金元素对纳米晶Fe3Al块体材料的磁性能影响明显.
The bulk nanocrystalline Fe3A1 and Fe3AI with NilOwt%, Cr10wt%, MnlOwt% and NilOwt% - Cu2wt% elements were prepared by aluminothermic reaction, respectively. The hysteresis loop was measured by vibrating sample magnetometer (VSM) ,the crystal structures of the samples were characterized by X - ray diffractometer (XRD) and the average grain sizes were calculated. Results show that the magnetic hysteresis loop of the alloys have tilting shape and long narrow, which indicates that the hysteresis loss is small. The satu- ration magnetization Ms of the Fe3A1 with 10wt% Ni is larger and the residual magnetization Mr and coercivity He are smaller than those of other alloys and demonstrate good soft magnetic property. The grain size of Fe3 A1 becomes Smaller after adding alloying elements, but the magnetic property changes a lot. It could be concluded that the effect of alloying elements on OUS. magnetic property of nanocrystalline Fe3 A1 based materials is obvi-
参考文献
| [1] | 古安林,薛屺,张进,刘玉宏.Fe3Al基金属间化合物涂层的研究进展[J].材料导报,2009(z1):457-460. |
| [2] | 薛飞,刘江南,严文.Fe3Al金属间化合物研究现状与发展[J].西安工业学院学报,2000(01):67-72. |
| [3] | 范润华,尹文宗,孙康宁,孙家涛,张玉军.无序化对有序铁铝金属间化合物磁性的影响[J].人工晶体学报,2005(04):606-609. |
| [4] | Zhang ZR;Liu WX .Mechanical properties of Fe3Al-based alloys with addition of carbon, niobium and titanium[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2006(1-2):343-349. |
| [5] | 陈国良.金属间化合物结构材料研究现状与发展[J].材料导报,2000(09):1-5. |
| [6] | 喇培清,赵阳,程春杰.Mn添加对铝热反应制备的块体纳米晶Fe3Al组织的影响[J].材料导报,2009(z1):50-52,60. |
| [7] | 喇培清,王利,赵阳,程春杰.底材厚度对铝热反应熔化制备的块体纳米晶Fe3Al材料的组织和性能的影响[J].兰州理工大学学报,2008(03):5-8. |
| [8] | W. Y. Peng;J. H. Zhang .Magnetostriction studies in an antiferromagnetic polycrystalline Mn_(42)Fe_(58) alloy[J].Applied physics letters,2006(26):262501-1-262501-3-0. |
| [9] | 杨王玥,盛丽珍,黄原定,毛卫民,孙祖庆.代位合金元素对Fe3Al金属间化合物结构与塑性的影响[J].中国有色金属学报,1996(04):101-105. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%