本工作研究了两种Ti_3Al(α_2基)金属间合金(Ti22Al-2Mn,Ti26Al-4Nb)粉末包装渗铝涂层及其900℃恒温与循环氧化行为。通过渗铝处理,在合金表面可获得与基体结合良好的TiAl_3涂层,以NH_4F作活化剂,经800℃,2h渗铝后,含Mn合金上的渗铝层界面平直,厚度均匀,约3μpm厚。在相同条件下,含Nb合金上的渗层界面呈波浪形,厚度不均匀。两种合金上的渗铝层都存在贯穿裂缝。经900℃恒温与循环氧化实验测定了渗铝与未渗铝合金的氧化动力学,渗铝后合金的抗氧化性能显著提高,讨论了渗铝层的
Two Ti_3Al(α_2) intermetallics, Ti22Al-2Mn and Ti26Al—4Nb, were aluminized by pack cementation process and the oxidation behavior at 900℃ was studied. An adherent TiAl_3 coating was obtained on the two intermetallics by the aluminization. The TiAl_3 coati