A kind of CWAO catalyst, RuO2/γ-Al2O3, was prepared by dipping Al2O3 into the aqueous solution of RuCl3.3H2O. XRD, SEM and TEM were used to determine the catalytic structure. Influences of the calcination temperature,the initial pH of the feed solution and degradation temperature on the activity of the RuO2/γ-Al2O3 catalyst were investigated and the reaction mechanism was preliminarily studied. Results showed that uniform dispersion of RuO2 crystallites was observed on the surface of the catalyst. The activity of the catalyst was higher at calcination temperature of 300℃ for 3 h and the particle reunion occurred and some large RuO2 crystallites were abundant at high calcination temperature of 500℃. The activity of the catalyst was better in the acid solution than in the alkaline solution. Increasing degradation temperature and using the catalyst could shorten the induction periods so that the phenol and COD removal were increased. For RuO2/γ-Al2O3 catalyst, the phenol and COD removal were respectively 98% and 80% in a temperature of 150℃, pH of 5.6 and pressure of 3 MPa after a 2 h reaction. This indicated that Ru/γ-Al2O3 catalyst had good activity.
参考文献
[1] | Wang Y T .Effect of chemical oxidation on anaerobic biodegradation of model phenolic compounds[J].Water Environment Research,1992,64:268. |
[2] | Lee S H;Carberry J.B .Biodegradation of PCP enhanced by chemical oxidation pretreatment[J].Water Environment Research,1992,64:682. |
[3] | Lanouette K H .Treatment of phenolic waste[J].Chemical Engineering,1997,17:99. |
[4] | Nie Y E;Liu F Q;Wang J J .Assessment on the way to develop incineration in China[J].Res of Envir Sci(in China),2000,13(03):20. |
[5] | Zimmermann E J .New waste disposal process[J].Chemical Engineering,1958,65:117. |
[6] | Vedprakash S. Mishra;Vijaykumar V. Mahajani;Jyeshtharaj B. Joshi .Wet Air Oxidation[J].Industrial & Engineering Chemistry Research,1995(1):2-48. |
[7] | Lin S H;Ho S.J .Catalytic wet air oxidation of high strength industrial wastewater[J].Applied Catalysis,1996,B9:133. |
[8] | Mantzavinous D;Hellenbrand R;Livingston A.G;Metcalfe I.S .Catalytic wet air oxidation of polyethylene glycol[J].Applied Catalysis,1996,B11:99. |
[9] | Dhale A D;Mahajani V.V .Studies in treatment of disperse dye waste: mambrane-wet oxidation Process[J].Water Management,2000,20:85. |
[10] | Levec J;Pintar A .Catalytic oxidation of aqueous solution of organic A: effective method for removal of toxic pollutants from wastewater[J].Catalysis Today,1995,24:51. |
[11] | Zhang Qinlin;Chuang Karl T .Kinetics of wet oxidation of black liquor over a Pt-Pd-Ce/alumina catalyst[J].Applied Catalysis,1998,B17:321. |
[12] | Maugans C B;Akgerman A .Catalytic wet oxidation of phenol over a Pt/TiO2 catalyst[J].Water Research,1997,17:3116. |
[13] | Qin J Y;Aika K .[J].Applied Catalysis,1998,B16:261. |
[14] | Barbier J Jr;Delanoe F;Jabouille F;Duprez D.,Blanchard G.,Isnard,P. .Total oxidation of acetic acid in aqueous solution over noble metal catalysts[J].Journal of Catalysis,1998,177:378. |
[15] | Sadana A;Katzer J.R .Catalytic oxidation of phenol in aqueous solution over copper oxide[J].Industrial and Engineering Chemistry Research,1974,13:127. |
[16] | Pintar A;Levec J .Catalytic liquid phase oxidation of refractory organics in wastewater[J].Chemical Engineering Science,1992,47:2395. |
[17] | Harmsent J M A;Jelemensky L;Van Andel-Scheffer P.J.M;Kuster B.F.M.,Martin G.B .Kinetic modeling for wet air oxidation of formic acid on a carbon supported platiinum catalyst[J].Applied Catalysis,1997,A165:449. |
[18] | Zhang Q L;Chuang K.T .Wetoxidationofbleachplanteffluents:effectofpHontheoxidationwithorwithoutaPd/Al2O3catalyst[J].Canadian Journal of Chemical Engineering,1999,77:399. |
[19] | Miro C;Alejanre A;Fortuny A .Aqueous phase catalytic of phenol in a trickle bed reaction: effect of the pH[J].Water Research,1999,33:1005. |
[20] | Mantzavinous D;Hellenbrand R;Livingston A.G;Metcalfe I.S .Catalytic wet oxidation of pcoumaric acid: partial oxidation, intermediates reaction pathways and catalyst leaching[J].Applied Catalysis,1996,B7:379. |
[21] | Willms S R;Balinsky A.M;Reible D.D;Harrison D.P .Analysis of high-pressure,mulfiphase reactor design[J].Environmental Progress,1985,4:131. |
[22] | Willms S R;Balinsky A M;Reible D D;Harrison D.P .Aqueous-phase oxidation:the kinetic of single organic compounds[J].Industrial and Engineering Chemistry Research,1987,26:148. |
[23] | Joglekar H S;Smant, S.D;Joshi J.B .Kinetics of wet air oxidation of phenol and substituted Phenol[J].Water Research,1991,25:135. |
[24] | Thomsen AB. .Degradation of quinoline by wet oxidation-kinetic aspects and reaction mechanisms[J].Water research: A journal of the international water association,1998(1):136-146. |
[25] | Karpel V;Leitner N;Dore M .[J].Water Research,1997,31:1383. |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%