以粗孔球形硅胶为载体，以聚乙二醇和二乙醇单乙醚的钛酸四丁酯无水乙醇溶液为浸涂液，用涂覆法制备了TiO2/SiO2光催化剂.用XRD，SEM和UV-Vis等对催化剂的物相、形貌及TiO2负载量进行了表征，并通过可溶性染料活性艳红X-3B的降解反应，考察了其光催化活性.实验结果表明，当选用16.79%TiO2/SiO2光催化剂时，活性艳红X-3B溶液的脱色率可达93%以上.
TiO2/SiO2 thin film was prepa red by repeating the followingprocedure， first dipping porous round silica gel in Ti-solution of tetrabutyl titanium ethanol containing polyethylene glycol a nd diethylene glycol monoethylether, then calcinating at 600 ℃ for 2 h. The cry stal phase, the morphology, and the TiO2 amount on the beads were determined b y XRD, SEM, and UV-Vis, respectively. The photocatalytic activity of TiO2/SiO2 th in film with different TiO2 loadings was evaluated by degradation of dye X-3 B in aqueous solution. In comparison of TiO2/SiO2 containing w(TiO2)= 54.02% with that containing w(TiO2)=16.79%, the former has larger ave rage particle diameter and had undergone some phase transformation from anatase to r util e, but no phase transformation had been observed for the latter. Furthermore, wi th 16.79%-TiO2/SiO2 as a catalyst, the degradation of dye X-3B in aqueous solution with O2 flow had a decolorization ratio up to 93% in 1h.
参考文献
| [1] | Fujishima A .[J].Chemistry(Japan),1999,54(03):14. |
| [2] | 沈伟韧,赵文宽,贺飞,方佑龄.TiO2光催化反应及其在废水处理中的应用[J].化学进展,1998(04):349-361. |
| [3] | 韩兆慧,赵化侨.半导体多相光催化应用研究进展[J].化学进展,1999(01):1-10. |
| [4] | Sandelle B.Chemical Analysis,Vol Ⅲ[M].New York:Inter-sci Publ,1959 |
| [5] | Cullity B D.Elements of X-Ray Diffraction 2nd Ed[M].Reading (Mass):Addison-Wesley,1978:102. |
| [6] | Spurr R A;Myers H .[J].Analytical Chemistry,1957,29(05):760. |
| [7] | Nishikawa H;Takahara Y .[J].Inorganic Materials(Japan),1999,6(07):291. |
| [8] | Yamashita H;Matsuoka M;Tsuji K .[J].Journal of Physical Chemistry,1996,100(01):397. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%