Li1+2x+yAlxNdyTi2-x-ySixP3-xO12 锂快离子导体（以下简称Al-Nd-Lisicon）可以用精选的天然高岭石Al4[Si4O10]（OH）8为起始原料，经与Li2CO3、TiO2、NH4H2PO4进行高温（800～1000℃）固相反应约20h而制得.一个空间群属于R3c的固溶体导电相可在y=0．5，x≤0.3和y=1.0，x≤0．4的组成范围内发现.该相具有较好的电导性和较低的活化能．起始组成y=1．0,x=0．3的合成物具有最高的电导率，在400℃时；其电导率达到3．08×10-2S／cm，离子导电激活能为35．2kJ／mol.
Natural layered aluminosilicate kaolinite Al4[Si4O10](OH)8 was used as a starting material for perparing a new system of lithium fast ion conductors
Li1+2x+yAlxNdyTi2-x-ySixP3-xO12 by high temperature (800～1000℃) solid phase reaction for about 20h. A solid solution phase with R3c structure exists in a
limited composition region. The electrical measurements indicated that the maximum conductivity in the above system (referred to as Al-Nd-Lisicon) is
the initial composition with x=1.0, x=0.3, its conductivity reaches up to 3.08×10-2S/cm at 400℃ and the activation energy is 35.2kJ/mol.
参考文献
| [1] | Fan Y, Wu H. The proceedings of 6th International Conference on Solid State Ionics (extended abstracts), 1987. 21. 2 俞文海, 王大志等. 无机材料学报, 1987, 2 (1): 82. 3 朱斌, 俞文海. 无机材料学报, 1988, 3 (3): 258. 4 Wang D, Yu W, et al. Solid State Ionics, 1989, 34: 219. 5 林枫凉. 电池, 1990, 20 (6): 26 和 1991, 21 (1): 22. 6 张志斌, 王文继等. 功能材料, 1993, 24 (1): 38. 7 Wang Wenji, Chem Jingxi. In: Chowdari B. V. R. ed. Solid State Ionics: Materials and Applications. W. S. Publishing Co., 1992. 369. 8 Wang Wenji, Huang Jiandong. In: Chowdari B. V. R. ed. Solid State Ionic Materials. W. S. Publishing Co., 1994. 179. 9 Wang Wenji, Li Duanyang. Ceylon J. of Science, 1995, 2 (1): 26. 10 王文继, 黄剑东. 无机材料学报, 1996, 11 (1): 119. 11 郭常霖, 黄月鸿. 物理学报, 1981, 30 (1): 124. 12 戴安邦, 沈孟光. 元素周期表. 上海: 上海科技出版社, 1978. 13 Hong T Y P. Mat res. Bull., 1976, 11: 173. 14 潘兆橹主编. 结晶学与矿物学(下册). 北京: 地质出版社, 1989. 173. 15 林祖纕, 李世椿等. 中国科学, 1984, A辑, 381. |