低碳铝镇静钢（LCAK）常用于生产冷轧板,要求铸坯有高的洁净度。但连铸开浇阶段由于浇铸状态的不稳定,会严重恶化头坯洁净度。从铸坯成分和非金属夹杂物等方面系统研究了一定浇铸条件下低碳铝镇静钢头坯洁净度的变化,并讨论了头坯洁净度的影响因素。结果表明,头坯洁净度在开浇准数达到0.17后趋于稳定,这可为实际生产中铸坯质量评级提供帮助。研究发现恶化头坯洁净度的主要因素是中间包二次氧化,并且除了由空气造成的中间包二次氧化外,更大程度上的二次氧化是由中间包耐火材料及覆盖渣等因素造成的。还提出了几点改善头坯洁净度的措施,为生产实践提供一定的参考。
High cleanliness is required for low carbon aluminum killed（LCAK for short） steel which is widely used for production of cold rolled sheet.But,head slab cleanliness is seriously deteriorated by the unsteady casting condition at casting start stage.Cleanliness of LCAK steel head slab was systemically investigated on aspects of slab composition and non-metallic inclusions under the present casting conditions.Besides,factors affecting the cleanliness of head slab were discussed.A cast starting number is defined.The results show that the head slab cleanliness is unstable until the number reaches 0.17,which can help slab quality classification.The main factor deteriorating head slab is the reoxidation in tundish.Besides oxygen in the air,more extent of reoxidation is caused by the refractory and covering slag in tundish.Several measures of improving head slab cleanliness were put forward as well,which can provide certain reference on plant operations.
参考文献
| [1] | 张乔英,王新华,张立,唐海波,徐国栋.拉速变化对IF钢铸坯非金属夹杂物含量的影响[J].炼钢,2006(06):21-26. |
| [2] | 张乔英,王立涛,王新华,王万军,李宏.非稳态浇铸时IF钢铸坯表层夹杂物粒径的分布[J].特殊钢,2006(05):9-11. |
| [3] | ZHANG Qiao-ying,WANG Li-tao,WANG Xin-hua,LI Hong,WANG Wan-jun.Non-Metallic Inclusion Distribution in Surface Layer of IF Steel Slabs[J].钢铁研究学报（英文版）,2008(01):70-74. |
| [4] | ZHANG Qiaoying;WANG Litao;WANG Xinhua et al.In- fluence of Casting Speed Variation during Unsteady Continous Casting on Non-metallic Inclusions in IF Steel Slabs[J].ISIJ International,2006,46(10):1421. |
| [5] | 孙彦辉,蔡开科,赵长亮.非稳态浇注操作对连铸坯洁净度影响[J].钢铁,2008(01):22-25. |
| [6] | 袁方明,王新华,李宏,任子平,张富强,孟劲松,孙群.不同浇铸阶段IF钢连铸板坯洁净度[J].北京科技大学学报,2005(04):436-440. |
| [7] | H. Jacobi;K. Wunnenberg .Improving oxide cleanness on basis of MIDAS method[J].Ironmaking & Steelmaking: Products and applications,2003(2):130-141. |
| [8] | Lifeng ZHANG;Brian G. THOMAS .State of the Art in Evaluation and Control of Steel Cleanliness[J].ISIJ International,2003(3):271-291. |
| [9] | Yuji Miki;Shuji Takeuchi .Bubble Entrapment on Solidified Shell caused by Unsteady Steel Flow in Mold[J].Steel Research,2003(2):114-118. |
| [10] | Hamill I;Lucas T.Fluid Flow Phenomena in Metals Pro- cessing[M].Warrendale,PA:Minerals,Metals and Materi als Society,1999:279. |
| [11] | Toshio TESHIMA;Jun KUBOTA;Mikio SUZUKI et al.Influence of Casting Conditions on Molten Steel Flow in Con tinuous Casting Mold at High Speed Casting of Slabs[J].Tetsu To Hagane-Journal of the Iron and Steel Institute of Japan,1993,79(05):576. |
| [12] | Wataru Ohashi,Takehiko Toh,Tooru Matsumiya.连铸工艺中弯月面控制的发展[J].钢铁,2004(z1):482-485. |
| [13] | 政冈俊雄;田口静夫;纳雅夫;ほか .连统铸造にぉける最ボトム铸片の品质改善[J].铁と钢,1987,73(12):S967. |
| [14] | Bessho N;Yamasaki H;Fujii T et al.Removal of Inclusion from Molten Steel in Continuous Casting Tundish[J].ISIJ International,1992,32(01):157. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%