采用不同单体浓度的聚苯胺包覆碳微球与PET共混后制得PANFCMSs/PET阻燃复合材料,研究了单体浓度对阻燃复合材料性能的影响,同时分析了复合材料的力学性能、阻燃性能及导电性能.结果表明:当单体浓度为1.5 mol/L时,阻燃复合材料的拉伸强度达到39.78MPa,冲击强度为3.48 kJ/m2,此时电阻率最低,导电性能最好,极限氧指数达到32.02％,PET的阻燃性能提高47.6％.
参考文献
| [1] | Anoop A K .Carbon nanotubes induced crystallization of poly(ethylene terephthalate)[J].POLYMER,2006,47(7):3976. |
| [2] | 张启路,马晓燕,李冬梅,屈小红,寇开昌.共混聚合物界面相容性研究进展[J].合成树脂及塑料,2010(01):80-83. |
| [3] | 武荣瑞.PET/碳纳米管共混物的研究进展[J].合成纤维工业,2012(06):32-37. |
| [4] | 陈汉周,刘钦甫,赵庆章,杨宇,高建辉.高岭土对PET结晶性能及热稳定性的影响[J].纺织科学研究,2008(02):9-13,18. |
| [5] | Carosio, F.;Alongi, J.;Frache, A. .Influence of surface activation by plasma and nanoparticle adsorption on the morphology, thermal stability and combustion behavior of PET fabrics[J].European Polymer Journal,2011(5):893-902. |
| [6] | Frisk P;Laurent J .Nanocomposite polymer container[P].US,5876812,1999. |
| [7] | TAKASHI KASHIWAGI;FANGMING DU;JACK F.DOUGLAS;KAREN I.WINEY;RICHARD H.HARRIS Jr. .Nanoparticle networks reduce the flammability of polymer nanocomposites[J].Nature materials,2005(12):928-933. |
| [8] | 罗瑞盈,向巧,李进松,章劲草.先进碳/碳复合飞机刹车材料关键技术研究和应用进展[J].航空制造技术,2010(01):56-58. |
| [9] | 孙迎辉,张慧东,叶开其,张晶莹,李伟,杨柏,王悦.基于分子间π-π相互作用形成的吖啶荧光化合物超分子结构及其性能研究[J].高等学校化学学报,2005(10):1865-1868. |
| [10] | 傅思睿;杨静晖.碳纳米管改性聚苯硫醚熔融纺纤维的结构与性能研究[J].高分子学报,2012(3):347. |
| [11] | Narendra V. Bhat;Devender T. Seshadri;Ratna S. Phadke .Simultaneous polymerization and crystallization of aniline[J].Synthetic Metals,2002(2):185-192. |
| [12] | 曾汉明;王苏平.功能纤维[M].北京:化学工业出版社,2005:268. |
| [13] | Lewis I C .Thermotropic mesophase pitch[J].CARBON,1978,16(6):503. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%