Influence of Solidification Rate on Microstructures of Cast Strips and Corresponding Sintered NdFeB Magnets

稀土学报(英文版), 2006, 24(z2): 306-309.

^1, , ^2, , ^3, , ^4, , ^5, , ^6,

1.National Engineering Research Center for Rare Earth Materials, General Research Institute for Nonferrous Metals, and Grirem Advanced Materials Co. Ltd., Beijing 100088, China

2.National Engineering Research Center for Rare Earth Materials, General Research Institute for Nonferrous Metals, and Grirem Advanced Materials Co. Ltd., Beijing 100088, China

3.National Engineering Research Center for Rare Earth Materials, General Research Institute for Nonferrous Metals, and Grirem Advanced Materials Co. Ltd., Beijing 100088, China

4.National Engineering Research Center for Rare Earth Materials, General Research Institute for Nonferrous Metals, and Grirem Advanced Materials Co. Ltd., Beijing 100088, China

5.National Engineering Research Center for Rare Earth Materials, General Research Institute for Nonferrous Metals, and Grirem Advanced Materials Co. Ltd., Beijing 100088, China

6.National Engineering Research Center for Rare Earth Materials, General Research Institute for Nonferrous Metals, and Grirem Advanced Materials Co. Ltd., Beijing 100088, China

基金项目: RE Application Engineering of National Ten-Fifth Year Plan of China(2002BA315A-1)

Influence of Solidification Rate on Microstructures of Cast Strips and Corresponding Sintered NdFeB Magnets

Keywords： sintered NdFeB magnets

The influences of solidification rate on the microstructures of cast strips and corresponding sintered NdFeB magnets were investigated. The experimental results show that the volume fraction and size of columnar grains vary with the wheel speed V, and the fraction is highest to more than 90% with 3.5 μm in average width at V＝2 m·s-1. The reasons for the improved magnetic performance were discussed based on the micromagnetic theory and microstructure analyses of the strips and sintered magnets. The magnetic properties of sintered NdFeB magnets made from the (Nd,Dy)13.0(Fe,Ga,Al)80.5B6.5 cast strip which was obtained at V=2 m·s-1 are as follows: Br=1.15 T(11.25 kG), iHc=2799 kA·m-1 (35.2 kOe) and (BH)max=242 kJ·m-3(30.35 MGOe).

参考文献

[1]	Sagawa M;Fujimura S;Togawa N et al.[J].Journal of Applied Physics,1984,55:2083.
[2]	Schneider G;Henig E T;Petzow G et al.[J].,1986,77:755.
[3]	Fidler J;Knoch K G .[J].Journal of Magnetism and Magnetic Materials,1989,80:48.
[4]	Rodewald W et al.[J].IEEE Transactions on Magnetics,2002,38:2955.
[5]	Bernardi J.;Sagawa M.;Hirose Y.;Fidler J. .Microstructural analysis of strip cast Nd-Fe-B alloys for high (BH)(max) magnets[J].Journal of Applied Physics,1998(11 Pt.2):6396-6398.
[6]	Kronmuller H.Hard Magnetic Materials[M].Nether lands:Kluwer Academic,1991:4.

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

Influence of Solidification Rate on Microstructures of Cast Strips and Corresponding Sintered NdFeB Magnets

参考文献