采用真空热压烧结工艺直接烧结Fe、Si混合粉末,制备了Fe3Si金属间化合物.研究了热压烧结时间对烧结产物微观结构、硬度及致密度的影响.结果表明,经950℃、22MPa热压烧结0.5～4h均可得到高度有序的Fe3Si块体,且随烧结时间的延长,烧结产物中Fe3Si的含量有所增加,但当烧结时间长于2h,Fe3Si的有序度有所降,低.同时烧结产物的硬度和密度也有同样的变化规律,其中烧结时间2h时烧结产物具有最佳硬度和密度,分别为90.7HRC和4.62g/m3.
参考文献
| [1] | Arai K I;Ohmori K;Tsuya N .Effect of order-disorder transition on magnetic properties of high silicon-iron single crystal[J].Journal of Applied Physics,1985,57(02):460. |
| [2] | Namikanwa M;Ninomiya H;Tanaka Y .Magnetic properties of 6.5 ％ sillicon steel sheets under PWN voltage excitation[J].IEEE Transactions on Magnetics,1988,34(04):1183. |
| [3] | Tanaka Y;Takand Y;Abe M et al.Magnetic properties of 6.5％ Si-Fe sheet and its application[J].Journal of Applied Physics,1990,83(01):375. |
| [4] | 周琦,赵红顺,贾建刚,马勤,邹欣伟.Fe3Si基金属间化合物的研究进展[J].甘肃科学学报,2007(04):29-33. |
| [5] | Ning Jiangtian;Yi Danqing .Study on Fe3Si intermetallics by mechanical alloy[J].Hunan Nonferrous Metals,2000,16(06):21. |
| [6] | Schneeweiss O.;Jiraskova Y.;Zak T.;Cornut B.;Pizurova N. .Fe3Si surface coating on SiFe steel[J].Journal of Magnetism and Magnetic Materials,2000(0):115-117. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%