采用溶胶-凝胶法制备SiO2气凝胶,以三甲基氯硅烷/环己烷、二甲基二氯硅烷/环己烷体系为化学表面修饰剂,通过衍生法制备了疏水性SiO2气凝胶.利用气质联用对表面改性过程中发生的反应进行了剖析;并利用扫描电镜、红外光谱、比表面测定等测试方法对2种改性方法所获得的SiO2气凝胶的结构、形貌及性能组成进行了比较.研究表明,2种改性方法均可获得连续网络结构、多孔纳米材料.所得SiO2气凝胶的比袁面积分别为652m2/g和656m2/g,主要孔径尺寸为2～10nm.样品表面连有疏水基团,呈现明显的疏水性.
参考文献
| [1] | Reim M et al.Silica aerogel granulate material for thermal insulation and daylighting[J].Journal of Solar Energy Engineering,2005,79:131. |
| [2] | Reim M;Reichenauer G;Korner W;Manara J;Arduini-Schuster M;Korder S;Beck A;Fricke J .Silica-aerogel granulate - Structural, optical and thermal properties[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,2004(0):358-363. |
| [3] | 张娜,张玉军,于延军,田庭艳.SiO2气凝胶制备方法及隔热性能的研究进展[J].陶瓷,2006(01):24-26. |
| [4] | 何飞,赫晓东,李垚.气凝胶热特性的研究现状[J].材料导报,2005(12):20-22. |
| [5] | Soleimani Dorcheh A;Ahbasi M H .Silica aerogel:synthesis,properties and characterization[J].Journal of Materials Processing Technology,2008,199:10. |
| [6] | 高秀霞,张伟娜,任敏,朱果逸.硅气凝胶的研究进展[J].长春理工大学学报（自然科学版）,2007(01):86-91. |
| [7] | Hoffmann H;Meyer M;Zeitler I .Control of morphology inside the mesoporous gelstructure in silica-gels[J].Colloids and Surfaces, A. Physicochemical and Engineering Aspects,2006(1/3):117-127. |
| [8] | 陈姚,于欣伟,钟智欣,胡家聪,谭英立.新型疏水沉淀二氧化硅的制备[J].无机盐工业,2005(02):18-20. |
| [9] | 殷吉超,彭晓峰,朴英.隔热材料的纳米成型与性能分析[J].工程热物理学报,2007(05):832-834. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%