为了缩短贝氏体转变时间并减少生产成本,设计并冶炼了一种新的贝氏体钢种,在Gleebe-1500热模拟实验机上测定其热膨胀曲线,结合显微组织图绘制了实验钢的CCT曲线。根据CCT曲线进行低温等温转变实验,对热处理试样进行拉伸试验,获得了实验钢低温转变后的力学性能。通过TEM观察发现低温转变的实验钢是由亚纳米级的超细贝氏体、马氏体等组成的一种超细贝氏体钢。340℃×2 h的低温等温转变,实验钢的抗拉强度达到1470 MPa,伸长率为15%。
参考文献
| [1] | F. G. Caballero;H. K. D. H. Bhadeshia;K. J. A. Mawella .Design of novel high strength bainitic steels: Part 1[J].Materials Science and Technology: MST: A publication of the Institute of Metals,2001(5):512-516. |
| [2] | F. G. Caballero;H. K. D. H. Bhadeshia;K. J. A. Mawella .Design of novel high strength bainitic steels: Part 2[J].Materials Science and Technology: MST: A publication of the Institute of Metals,2001(5):517-522. |
| [3] | F.G. Caballero;M.J. Santofimia;C. Garcia-Mateo;J. Chao;C. Garcia de Andres .Theoretical design and advanced microstructure in super high strength steels[J].Materials & design,2009(6):2077-2083. |
| [4] | F. G. Caballero;H. K. D. H. Bhadeshia;K. J. A. Mawella .Very strong low temperature bainite[J].Materials Science and Technology: MST: A publication of the Institute of Metals,2002(3):279-284. |
| [5] | 黄维刚,方鸿生,郑燕康.C-Si-Mn-B系贝氏体钢的强度及强化机制[J].钢铁研究学报,2003(01):38-41. |
| [6] | 康永林,陈庆军,王克鲁,孙浩,于浩.700MPa级低碳贝氏体钢的热处理工艺研究[J].材料热处理学报,2005(03):96-99. |
| [7] | Irvine K J;Picketing F B .Low carbon bainitic steels[J].Journal of the Iron and Steel Institute,1957,184(12):292-309. |
| [8] | 王六定,朱明,陈景东,施易军,陈国栋.低碳超高强度贝氏体钢的组织细化[J].材料热处理学报,2007(05):42-45. |
| [9] | Caballero FG;Bhadeshia HKDH .Very strong bainite[J].Current opinion in solid state & materials science,2004(3/4):251-257. |
| [10] | 高宽,王六定,朱明,陈景东,施易军,康沫狂.低合金超高强度贝氏体钢的晶粒细化与韧性提高[J].金属学报,2007(03):315-320. |
| [11] | 武会宾,尚成嘉,苑少强,杨善武,王学敏,贺信莱.超细化低碳贝氏体钢的回火组织稳定性及力学性能[J].材料热处理学报,2004(06):65-70. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%