用静电纺丝法制备了纤维平均直径为350～1900nm的聚乳酸纤维,用扫描电镜研究了纤维的形貌,并用实验设计方法研究了纺丝工艺参数(溶液浓度、电场电压)对纤维平均直径的影响,同时用差示扫描量热分析和X射线衍射研究了静电纺丝所得纤维的结构.研究结果表明:溶液浓度对纤维的平均直径有较大的影响,溶液浓度较低时易形成珠状结构的纤维,纤维的平均直径随着聚合物浓度的增大而增大,并随电场电压的增大而减小.与浇铸膜相比,静电纺丝所制得的纤维有较低的结晶度,并且结晶结构不够完善.由静电纺丝制备的聚乳酸纳米纤维膜在组织工程和药物缓释等领域有潜在的应用前景.
参考文献
| [1] | Gogolewski S;Pineda L;Busing C M .Bone regeneration in segmental defects with resorbable polymeric membrane Ⅳ.Does the polymer chemical composition affect the healing process[J].Biomaterials,2002,21:2513. |
| [2] | Ma PX;Choi JW .Biodegradable polymer scaffolds with well-defined interconnected spherical pore network.[J].Tissue engineering,2001(1):23-33. |
| [3] | Mooney D J;Mazzonic T;Breuer C et al.Stabilized poly(glycolic acid)fiber-based tubes for tissue engineering[J].Biomaterials,1996,17:115. |
| [4] | Nam YS;Park TG .Biodegradable polymeric microcellular foams by modified thermally induced phase separation method.[J].Biomaterials,1999(19):1783-1790. |
| [5] | Shin Y M;Hohman M M;Brenner M P et al.Experimental characterization of electrospinning:the electrically forced jet and instabilities[J].Polymer,2001,42:9955. |
| [6] | Boland E D;Wnek G E;Simpson D G et al.Tailoring tissue engineering scaffolds using electrostatic processing techniques:A study of poly(glycolic acid)electrospinning[J].Journal of Macromolecular Science:Chemistry,2001,38:1231. |
| [7] | Kim K;Yu M;Zong X;Chiu J;Fang D;Seo YS;Hsiao BS;Chu B;Hadjiargyrou M .Control of degradation rate and hydrophilicity in electrospun non-woven poly(D,L-lactide) nanofiber scaffolds for biomedical applications.[J].Biomaterials,2003(27):4977-4985. |
| [8] | Zeng J;Xu X;Chen X et al.Biodegradable elctrospun fibers for drug delivery[J].Journal of Controlled Release,2003,92:227. |
| [9] | Formhals A .Process and apparatus for preparing artificial thread[P].USP:1975504,1934. |
| [10] | Reneker D H;Yarin A L;Fong H et al.Bending instability of electrically charged liquid jets of polymer solutions[J].Journal of Applied Physiology,2000,87:4531. |
| [11] | Zong X;Kim K;Fang D et al.Structure and process relationship of electrospun bioabsorbable nanofiber membranes[J].POLYMER,2002,43:4403. |
| [12] | Demir MM.;Yilgor I.;Yilgor E.;Erman B. .Electrospinning of polyurethane fibers[J].Polymer: The International Journal for the Science and Technology of Polymers,2002(11):3303-3309. |
| [13] | Deitzel JM.;Harris D.;Tan NCB.;Kleinmeyer J. .The effect of processing variables on the morphology of electrospun nanofibers and textiles[J].Polymer: The International Journal for the Science and Technology of Polymers,2001(1):261-272. |
| [14] | Renker D H;Chun I .Nanometre diameter fibres of polymer,produced by electrospinning[J].NANOTECHNOLOGY,1996,7:216. |
| [15] | Mo XM.;Xu CY.;Kotaki M.;Ramakrishna S. .Electrospun P(LLA-CL) nanofiber: a biomimetic extracellular matrix for smooth muscle cell and endothelial cell proliferation[J].Biomaterials,2004(10):1883-1890. |
| [16] | Sukigara S;Gandhi M;Ayutsede J et al.Regeneration of bombyx mori silk byelectrospinning-Part 1:processing parameters and geometric properties[J].Polymer,2003,44:5721. |
| [17] | Zong X;Ran S;Fang D et al.Control of structure,morphology and property in electrospun poly(glycolide-co-lactide)non-woven membranes via post-draw treatments[J].Polymer,2003,44:4959. |
| [18] | Mun R P;Byars J A;Boger D V .The effect of polymer concentration and molecular weight on the breakup of laminar capillary jets[J].Journal of Non-Newtonian Fluid Mechanics,1998,74:285. |
| [19] | Nam P H;Maiti P;Okamoto M .Elongational flow birefringence of ethylene-tetracyclododecene copolymer[J].Polymer,2001,8:3939. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%