The effect of recrystallization annealing temperature on the properties and microstructure of one-step cold rolled steel strip for shadow mask was studied.The results showed that there was no yield point elongation when the tensile tests were performed on the samples for annealing temperatures ranging from 750℃ to 810 ℃.Moreover,increasing annealing temperature resulted in large grains,which was beneficial to the formability and magnetic property of steel strips.On the other hand,when the sample was annealed at 840 ℃,its microstructure showed ununifortuity with 0.04% yield point elongation,which was not good for the function of the shadow mask.Therefore,the proper recrystallization annealing temperature was about 810 ℃ for the present steel strip for shadow mask.
参考文献
| [1] | Kim G;Jin Y S.Decarburization Annealing of Extra-Low Carbon Steel for Shadow Mask[A].Charlotte:Country of Publication,2001:595. |
| [2] | Kim G S;Hwang H G;Kim E Y .Method for Manufacturing Cold Rolled Shadow Mask Steel Sheet With Stacked Annealing[P].US 6193819,2001-03-13. |
| [3] | Sato;Taizo;Ueda .Material for Shadow Mask,Method for Production Thereof,Shadow Mask and Image[P].US 6803712,2004-10-12. |
| [4] | LI Jun;CHEN Shou-qun;YAO Lin-long .Cold Rolled Sheet Steel for Shadow Mask and Manufacturing Method Therefore[P].CN 01113107.1,2002-01-09. |
| [5] | IEC Standard 404-7-1982.IEC Standard 404-7-1982.Magnetic Materials[S]. |
| [6] | Kim K S;Hwang H G;Kim E Y .Cold Rolled Steel Sheet for Shadow Mask Made by Low Temperature Annealing and Manufacturing Method Therefore[P].US 6117253,2000-09-12. |
| [7] | Jeong W C;Park C H;Park T Y .Cold Rolled Sheet Steel for Shadow Mask and Manufacturing Method Therefore[P].WO 9613618,1996-05-09. |
| [8] | A. J. DeArdo .Niobium in modern steels[J].International Materials Reviews,2003(6):371-402. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%