The mixing technology of laser and heated nitrogen was applied to improve the surface hardaccelerate the nitriding process. Some interested samples were tested with XRD method (X-ray diffraction) to analyze the composition of nitrides, and the surface hardness of HV was measured.The results show that TiN and Ti2N were formed on the surface of Ti alloy with proper nitriding parameters, but TiN is the main composition. The surface hardness increased by three times, which sidered mainly of the activation of nitrogen by laser power and the pre-heated process which accelerated the nitriding process. The nitridation process can be considered as six steps given in detail. The result by analyzing the mechanism of improving the surface property of TiAl alloy shows the improvement of surface property due to two factors: the first reason is the result of laser annealing, and the second one is the formation of TiN.
参考文献
| [1] | 汪洪海,郑启光,陶星之,王涛,辜建辉,何秀丽,王华明.大功率CO2激光原位直接反应合成TiN/Ti复合材料的研究[J].复合材料学报,1999(01):111-116. |
| [2] | I Gredic;M Latanoric;W D Münz .[J].Surface and Coatings Technology,1993,61:338. |
| [3] | A L Thomann;E Sicard;C Boulmer-Leborgne;C Vivien, I Hermann, C Andreazza-Xiqnolle, P Andeazza, C Meneau .[J].Surface and Coatings Technology,1997,97:448. |
| [4] | J D Wu;C Z Wu;X X Zhong;Z M Zong, F M Li .[J].Surface and Coatings Technology,1997,96:330. |
| [5] | D Xu;Z H Zheng;X H Liu;S X Zou, S Taniguchi, T Shibata, T Yamada .[J].Surface and Coatings Technology,1994,66:486. |
| [6] | 杨玉玲,孙凤久,张多.大气气氛下Ti表面激光氮化及其温度场的计算[J].激光技术,2005(02):201-204. |
| [7] | Y L Yang .[D].沈阳:东北大学,2002. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%