以钛稳定化的超纯Crl7铁素体不锈钢为研究对象，系统研究了精轧温度对铁素体不锈钢薄板屈服行为的影响。经高温精轧和低温精轧后，两种工艺的热轧板采用相同的退火及冷轧工艺得到成品薄板。采用低温精轧后，拉伸过程中薄板的Ltiders应变降低至0．5％左右，与高温精轧相比减少大约66．7％。通过金相显微组织观察、X射线衍射检测、内耗测量及TEM观察，结果表明：与高温精轧相比，低温精轧有利于细化及均匀化成品板的组织；低温精轧有利于细小球形析出相TiC的形成，降低基体中固溶间隙原子的含量，导致低温精轧后成品板Ltiders应变的减少。这与成品板内耗谱变化相一致。
The influence of finish rolling temperature on yield behavior in ultra purified ferritic stainless steels stabilized with titanium has been investigated. The hot rolled bands, which were finish rolled at high and low temperatures, were annealed and cold rolled in the same processes. And two final sheets with different finish rolling temperature were obtained. The final sheet at low temperature finish rolling exhibits a markedly reduced Luders elongation of only about 0.5 %, a decrease of about 66.7% over that at high temperature finish rolling during tensile testing. Through investigation by using optical microscopy observations, X-ray diffraction measurements, internal friction measurements and transmission electron microscopy observations, the results showed that low temperature finish rolling resulted in the refined rolling and annealing microstructure as compared to high temperature finish rolling l Low temperature finish rolling promoted the formation of a large number of fine TiC precipitates and reduces in large amount of interstitial atoms in solid solution, resulting in the much reduced Ltiders elongation. These results have been confirmed by the internal friction measurements.
参考文献
| [1] | Yoshihiro Yazawa;Yoshihiro Ozaki;Yasushi Kato;Osamu Furukimi .Development of ferritic stainless steel sheets with excellent deep drawability by (111} recrystallization texture control[J].JSAE review,2003(4):483-488. |
| [2] | Haitao LIU;Zhenyu LIU;Guodong WANG .Texture development and formability of strip cast 17% Cr ferritic stainless steel[J].ISIJ International,2009(6):890-896. |
| [3] | Filho A F;Herrera C;de Lima N B.Texture Evolu-tion of Ferritie(AISI 430)Stainless Steel Strips During Cold Rolling Annealing and Drawing[J].Materials Science Forum,2007(539-543):4926. |
| [4] | Almagro J F;Llovet X;Heredia M A et al.Soluble Frac-tion of Stabilizing Elements in Ferritie Stainless Steel[J].Mi-crochim Acta,2008,161(3-4):323. |
| [5] | Hu H .Effect of Solutes on Liiders Strain in Low-Carbon Steel Sheets[J].Metallurgical and Materials Transactions,1983,14(01):85. |
| [6] | Kazutake KOMORI .Analysis of Longitudinal Buckling in Temper Rolling[J].ISIJ International,2009(3):408-415. |
| [7] | 马庆龙,杨利坡,彭艳,刘宏民,吴斌.冷轧带钢平整时横折印缺陷的产生机理及消除措施[J].钢铁,2008(01):45-49. |
| [8] | 刘海涛,杜伟,谢胜涛,刘振宇,王国栋.初始凝固组织对Cr17铁素体不锈钢组织、织构及成形性的影响[J].钢铁研究学报,2008(10):32-35,62. |
| [9] | M.R.BARNETT .Influence of Ferrite Rolling Temperature on Microstructure and Texture in Deformed Low C and IF Steels[J].ISIJ International,1997(7):697-705. |
| [10] | Liu, Z.Y.;Gao, F.;Jiang, L.Z.;Wang, G.D. .The correlation between yielding behavior and precipitation in ultra purified ferritic stainless steels[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2010(16/17):3800-3806. |
| [11] | 毛新平.薄板坯连铸连轧微合金技术[M].北京:冶金工业出版社,2008 |
| [12] | M.R.BARNETT .Influence of Ferrite Rolling Temperature on Grain Size and Texture in Annealed Low C and IF Steels[J].ISIJ International,1997(7):706-714. |
| [13] | Golovin IS.;Schaller R.;Blanter MS. .SNOEK RELAXATION IN FE-CR ALLOYS AND INTERSTITIAL-SUBSTITUTIONAL INTERACTION[J].Physica Status Solidi, A. Applied Research,1997(1):49-60. |
| [14] | Eloot K;Kestens L;Dilewijns J .The Effect of Texture on the Height of the SnoOk Peak in Electrical Steels[J].ISIJ International,1997,37(06):615. |
| [15] | Saitoh H;Yoshinaga N;Ushioda K .Influence of Substitu-tional Atoms on the SnoOk Peak of Carbon in b.c.c.Iron[J].Acta Materialia,2004,52(05):1255. |
| [16] | Shin E;Seong B S;Kang H J et al.Textures and Precipi-tates in Ti-Stabilized Interstitial-Free Steel[J].Zeitschrift fur Metallkunde,2003,94(11):1234. |
| [17] | Nooning R G .Effect of Stabilizing Elements on the Precipita-tion Behavior and Phase Stability of Type 409 Ferritic Stain-less Steels[D].Thesis,University of Pittsburgh,2002. |
| [18] | M.Hua;C.I.Garcia .Precipitation Behavior in Ultra-Low-Carbon Steels Containing Titanium and Niobium[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,1997(9):1769-1780. |
| [19] | Pandit A;Murugaiyan A;Podder AS;Haldar A;Bhattacharjee D;Chandra S;Ray RK .Strain induced precipitation of complex carbonitrides in Nb-V and Ti-V microalloyed steels[J].Scripta materialia,2005(11):1309-1314. |
| [20] | Sun W P;Militaer M;Jonas J J .Strain-Induced Nucleation of MnS in Electrical Steels[J].Metallurgical and Materials Transactions,1992,23A(03):821. |
| [21] | Chang S K;Kang H J .Hot Driect Rolling in Ferrite Region in Extra Low-Carbon Steel[J].Steel Researeh International,1995,66(11):463. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%