为结合一维纳米材料和纳米颗粒复合材料的优点,本文尝试进行了在氧化铝模板(AAO)中生长Bi2Te3-SiO2纳米颗粒复合纳米线阵列.通过在电化学溶液中添加SiO2纳米颗粒,制备包含纳米颗粒的Bi-Te纳米线阵列.应用XRD、SEM、TEM等方法对合成的样品进行了分析观察.研究发现SiO2纳米颗粒的加入对纳米线的形貌和结构都有明显的影响.在模板法沉积Bi2Te3纳米线阵列时,添加SiO2纳米颗粒将明显改变纳米线生长方式,Bi2Te3纳米线不再是等径的纳米棒,而是枝晶生长过程,最后形成Z字型的不断反复弯折纳米线,该枝晶状纳米线的直径远小于模板的孔径.这一新颖的现象为制备直径更小,并具备精细界面结构的纳米线热电材料提供了一种新的可能途径.
参考文献
| [1] | Heremans J.;Thrush CM. .Thermoelectric power of bismuth nanowires[J].Physical Review.B.Condensed Matter,1999(19):12579-12583. |
| [2] | Zhaoping Liu;Shu Li;You Yang;Zhaokang Hu;Sheng Peng;Jianbo Liang;Yitai Qian .Shape-controlled synthesis and growth mechanism of one-dimensional nanostructures of trigonal tellurium[J].New Journal of Chemistry,2003(12):1748-1752. |
| [3] | Marisol Martin-Gonzalez;Amy L. Prieto;Ronald Gronsky;Timothy Sands;Angelica M. Stacy .High-Density 40 nm Diameter Sb-Rich Bi_2-Sb_xTe_3 Nanowire Arrays[J].Advanced Materials,2003(12):1003-1006. |
| [4] | Wei Wang;Qinghua Huang;Falong Jia;Jing Zhu .Electrochemically assembled p-type Bi_(2)Te_(3) nanowire arrays[J].Journal of Applied Physics,2004(1):615-618. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%