以硫酸钛为钛源,浓氨水为沉淀剂,通过水热水解法在240℃,48 h,pH=9时合成了粒径约为20 nm的锐钛矿TiO2纳米颗粒.利用X射线衍射仪(XRD)、热场发射扫描电子显微镜(SEM)、热场发射透射电子显微镜(TEM)和紫外可见分光光度计(UV-VIS)对试样进行分析.结果表明:硫酸钛溶液水热水解法不加入浓氨水时,随着水解时间的延长,虽然获得的锐钛矿型TiO2颗粒的粒径已达到了纳米级,但是其粒径的变化不明显;硫酸钛溶液水热水解法时加入浓氨水,合成锐钛矿型TiO2颗粒的粒径明显变小,但是,随着pH值的增加,合成锐钛矿型TiO2颗粒的粒径变化不明显.对不同条件下水热水解法合成的TiO2进行UV-VIS分析可得,TiO2颗粒粒径的变小有利于TiO2吸收峰的蓝移.
参考文献
| [1] | 赵宏生,胡红坡,张凯红,李自强.氮掺杂二氧化钛薄膜的制备与光催化性能[J].稀有金属材料与工程,2009(10):1815-1817. |
| [2] | Sreemany M.;Sen S. .A simple spectrophotometric method for determination of the optical constants and band gap energy of multiple layer TiO2 thin films[J].Materials Chemistry and Physics,2004(1):169-177. |
| [3] | Tayade RJ;Kulkarni RG;Jasra RV .Transition metal ion impregnated mesoporous TiO2 for photocatalytic degradation of organic contaminants in water[J].Industrial & Engineering Chemistry Research,2006(15):5231-5238. |
| [4] | Yang J.;Ferreira M.F. .Hydrothermal Synthesis of Nanosized Titania Powders: Influence of Peptization and Peptizing Agents on the Crystalline Phases and Phase Transitions[J].Journal of the American Ceramic Society,2000(6):1361-1368. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%