以Ni、Al元素粉末为原料,采用反应烧结工艺制备多孔NiAl金属间化合物材料,表征各烧结温度所对应的孔结构,研究NiAl烧结体的造孔机理.结果表明:在多孔NiAl金属间化合物材料的制备过程中,当温度在1100℃以下,随着烧结温度的升高,NiAl烧结体中的孔隙度和最大孔径呈现增大的趋势;经1100℃烧结之后,多孔NiAl的孔隙度为53%,最大孔径为55μm;造孔机理为Al熔点附近的Ni、Al之间的剧烈扩散造孔形成大量的开孔隙度,以及高温烧结阶段的Ni与中间相的扩散形成的多孔NiAl材料骨架中的孔洞.
@@@@The porous NiAl intermetallic was prepared using Ni, Al elemental powders as raw material through reaction sintering process, and the pore structures corresponding to the sintering temperature was also characterized. The results show that the porosity of porous NiAl intermetallic compounds during the preparation increases with the sintering temperature increasing. The porosity in the sintered body and the maximum pore size of porous NiAl are about 53%and 55μm, respectively, at 1 100℃. The pore formation mechanism of porous NiAl is that the large number of open porosity forms by the dramatic interdiffusion reaction between Ni and Al near the Al melting point temperature, and the porosity in the porous material skeletons forms by the interdiffusion reaction between the Ni and intermediates at high temperature.
参考文献
| [1] | K.Mark Thomas .Hydrogen adsorption and storage on porous materials[J].Catalysis Today,2007(3/4):389-398. |
| [2] | Y.H. Wang;J.P. Lin;Y.H. He .Pore structures and thermal insulating properties of high Nb containing TiAl porous alloys[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2010(1/2):213-218. |
| [3] | Zhang Bo;Chen Tianning .Calculation Of Sound Absorption Characteristics Of Porous Sintered Fiber Metal[J].Applied acoustics,2009(2):337-346. |
| [4] | Hideo Nakajima .Fabrication, properties and application of porous metals with directional pores[J].Progress in materials science,2007(7):1091-1173. |
| [5] | 邱克强,赵宇航,任英磊,张式程,张涛.Zr基非晶合金多孔材料的制备与性能[J].中国有色金属学报,2009(05):900-903. |
| [6] | 张学军,吴维(山文),牛焱.Ag对β-NiAl高温氧化膜Al2O3形貌的影响[J].金属学报,2005(04):369-374. |
| [7] | H. Latreche;S. Doublet;G. Tegeder;G. Wolf;P. Masset;T. Weber;M. Schutze .Behaviour of NiAl APS-coatings in chlorine-containing atmospheres[J].Materials and Corrosion,2008(7):573-583. |
| [8] | 吴杰,崔洪芝,曹丽丽,谷征征.以尿素为造孔剂制备开孔NiAl金属间化合物[J].中国有色金属学报（英文版）,2011(08):1750-1754. |
| [9] | A. Biswas;S. K. Roy;K. R. Gurumurthy .A study of self-propagating high-temperature synthesis of NiAl in thermal explosion mode[J].Acta materialia,2002(4):757-773. |
| [10] | DONG H X;HE Y H;ZOU J;XU N P HUANG B Y LIU C T .Effect of preheating treatment at 575℃ of green compacts on porous NiAl[J].Journal of Alloys and Compounds,2010,492:219-225. |
| [11] | H.X. Dong;Y. Jiang;Y.H. He .Formation of porous Ni-Al intermetallics through pressureless reaction synthesis[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2009(1/2):907-913. |
| [12] | CUI Hong-zhi;CAO Li-li;CHEN Yun-bo;WU Jie .Unique microstructure of porous NiAl intermetallic compoud prepared by combustion synthesis[J].Journa of Porous Materials,2012,19(04):415-422. |
| [13] | C. E. Campbell;W. J. Boettinger;U.R. Kattner .Development of a diffusion mobility database for Ni-base superalloys[J].Acta materialia,2002(4):775-792. |
| [14] | BOSE A;RABIN B H;GERMAN R M .Reactive sintering nickel-aluminide to near full density[J].Powder Metallurgy International,1988,20:25-30. |
| [15] | IKEDA T;ALMAZOUZI A;NUMAKURA H;KOIWA M SPRENGEL W NAKAJIMA H .Single-phase interdiffusion in Ni3Al[J].Acta Materialia,1998,46:5369-5376. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%