对掺杂ZnO-V2O5压敏电阻的低温烧结特性及电性能进行了研究.研究结果表明:通过添加硼酸铅锌玻璃“形成”氧化物PbO和B2O3使其在常规电烧结炉中的烧结温度降低到了800℃,并使非线性特性明显提高,添加6wt％(PbO+B2O3)的样品经800℃ 4h烧结后,其非线性系数和漏电流密度可分别达到22.5,7.2×10-6A/cm2.
The low-temperature sintering characteristics and electrical properties of ZnO-V2O5 varistors
were studied through adding oxides with low melting point, which were the lead zinc borate glass frit forming materials. The results show
that the sintering temperature is significantly decreased to 800℃ with conventional electric furnace sintering and the nonlinear
properties are obviously enhanced through adding B2O3 and PbO. When the sample with co-doped 6wt% (PbO+B2O3) sintered at 800℃ for 4h, its
leakage current density JL=7.2×10-6A/cm2 and nonlinear coefficient α=22.5.
参考文献
| [1] | Matsuoka M, Masuyama T, Iida Y. Jpn. J. Appl. Phys., 1969, 8: 1275--1276. [2] Wong J. J. Appl. Phys., 1980, 51 (8): 4453--4459. [3] Aldo B. Alles, and Vernon L. Burdick. J. Appl. Phys., 1991, 70 (11): 6883--6890. [4] Alles AIdo B, Puskas Robert, Callahan, et al. J. Am. Ceram. Soc., 1993, 76 (8): 2098--2102. [5] Caballero A C, Valle F J, Villegas M, et al. J. Europ. Ceram. Soc., 2000, 20 (16): 2767--2772. [6] Tsai Jyh-Kuang, Wu Tai-Bor. Mater. Lett., 1996, 26: 199--203. [7] Chen Chang-Shun, Kuo Cheng-Teu, Wu Tai-Bor, et al. Jpn. J. Appl. Phys., 1997, 36 (3A): 1169--1175. [8] Nobuaki Shohata, Junichirho Yoshida. Jpn. J. Appl. Phys., 1977, 16 (12): 2299--2300. [9] Lii Yih-Shing, Tseng Tseung-Yuen. J. Am. Ceram. Soc., 1992, 75 (6): 1636--1640. [10] Kurzawa M, I. Rychlowska-Himmel, Bosacka M, et al. J. Them. Anal. Cal., 2001, 64: 1113--1119. [11] Kuo Cheng-Tzu, Chen Chang-Shun, Lin I-Nan. J. Am. Ceram. Soc., 1998, 81 (11): 2942--2948. [12] Kuo Cheng-Tzu, Chen Chang-Shun, Lin I-Nan. J. Am. Ceram. Soc., 1998, 81 (11): 2949--2956. [13] Hng Huey Hoon, Kevin M. Knowles. J. Europ. Ceram. Soc., 1999, 9: 721--726. [14] Hng Huey-Hoon, Kevin M. Knowles. J. Am. Ceram. Soc., 2000, 83 (10): 2455--2462. [15] 陈树森译. 易熔玻璃, 第1版. 中国建筑工业出版社出版, 1975. 13. [16] Heli Jantunen, Risto Rautioaho, Antti Uusimaki, et al. J. Am. Ceram. Soc., 2000, 83 (11): 2855--2857. [17] 霍建华, 郭亚平, 刘琳娜. 传感器技术, 1998, 17 (6): 15--17. [18] 周东祥, 付~~明, 龚树萍, 等. 华中理工大学学报, 2000, 28 (3): 96--98 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%