将掺杂纳米Al2O3的聚酰胺酸与未掺杂聚酰胺酸在玻璃板上逐层涂膜,热亚胺化制备了3层聚酰亚胺/纳米Al2O3复合薄膜.采用扫描电镜(SEM)对该薄膜的微观形貌进行了表征,测试了薄膜的热稳定性、力学性能及电击穿场强.结果表明,复合薄膜的热性能及电击穿场强均高于掺杂薄膜及未掺杂膜,当热失重达到10%时,复合薄膜的热分解温度达到了629.1℃;与掺杂薄膜相比,复合薄膜的力学性能得到明显提高,拉伸强度和断裂伸长率分别为117.4 MPa和18.5%.
参考文献
| [1] | 李生柱,吴建华,朱小华,张樑.高性能聚酰亚胺的进展[J].化工新型材料,2002(06):19-24. |
| [2] | Qin JQ;Zhao H;Zhu RQ;Zhang XY;Gu Y .Effect of chemical interaction on morphology and mechanical properties of CPI-OH/SiO2 hybrid films with coupling agent[J].Journal of Applied Polymer Science,2007(6):3530-3538. |
| [3] | ZHANG Ming-yan,ZENG Shu-jin,DONG Tie-quan,ZHOU Sheng,FAN Yong,ZHANG Xiao-hong,LEI Qing-quan.Preparation and characterization of polyimide/silica hybrid films[J].哈尔滨工业大学学报（英文版）,2006(04):439-443. |
| [4] | 李鸿岩,郭磊,刘斌,陈维,陈寿田.聚酰亚胺/纳米Al2O3复合薄膜的介电性能[J].中国电机工程学报,2006(20):166-170. |
| [5] | Wu J T;Yang S Y;Gao S Q et al.[J].Polymer,2005,41:73-81. |
| [6] | Ma PC;Nie W;Yang ZH;Zhang PH;Li G;Lei QQ;Gao LX;Ji XL;Ding MX .Preparation and characterization of polyimide/Al2O3 hybrid films by sol-gel process[J].Journal of Applied Polymer Science,2008(2):705-712. |
| [7] | 刘立柱,高琳,宋玉侠,赵洪,雷清泉.偶联剂用量对聚酰亚胺杂化薄膜结构与性能的影响[J].功能材料,2008(05):814-816,820. |
| [8] | 李元庆,张以河,李明,付绍云.PI/T-SiO2杂化薄膜的制备及偶联剂的影响[J].合成树脂及塑料,2004(05):61-64. |
| [9] | 李传峰,钟顺和.溶胶凝胶法合成聚酰亚胺二氧化钛杂化膜[J].高分子学报,2002(03):326-330. |
| [10] | 高濂;孙静;刘阳桥.纳米粉体的分散及表面改性[M].北京:化学工业出版社,2002 |
| [11] | 曹晓珑,徐曼,刘春涛.纳米添加剂对聚合物击穿性能的影响[J].电工技术学报,2006(02):8-12. |
| [12] | 胡海兵,李鸿岩,刘斌.纳米填料对聚合物介电性能的影响[J].绝缘材料,2006(05):36-39. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%