在工业机组上制备了M2高速钢铸带,采用扫描电镜和透射电镜研究了热处理和热轧对铸带中的共晶碳化物特征的影响.结果表明:双辊薄带连铸工艺可以获得共晶碳化物尺寸细小、分布均匀的高速钢铸带,铸带中存在较多的M2C亚稳相碳化物;热处理后M2C碳化物分解生成M6C和MC碳化物,碳化物得到进一步细化;由M2工业铸带直接热轧而成的薄带中仍存在一些呈断续网状分布的碳化物,先进行合适的热处理再进行热轧对M2工业铸带更为合适.
参考文献
| [1] | 郭耕三.高速钢及其热处理[M].北京:机械工业出版社,1985 |
| [2] | 邓玉昆;陈景榕;王世章.高速工具钢[M].北京:冶金工业出版社,2002 |
| [3] | W. A. Opalka .Direct strip casting developments quicken[J].Iron & Steelmaker,1999(2):39-40. |
| [4] | Claus Hendricks .Strip casting technology---a revolution in the steel industry?[J].Metallurgical Plant and Technology International,1995(3):42-44,46,48-49-0. |
| [5] | Schueren M.The CASTRIP process-an update on process development at nucor steels first commercial strip castting facility[J].AIS Tech,2007(05):7-10. |
| [6] | Hohenbichler G.EUROSTRIP-direct strip casting of carbon and stainless steel[A].,2002:14-16. |
| [7] | Pan F;Zhou S;Ding P et al.Thin strip casting of high speed steels[J].Journal of Materials Processing Technology,1997,63(03):792-796. |
| [8] | M. Boccalini;H. Goldenstein .Solidification of high speed steels[J].International Materials Reviews,2001(2):92-115. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%