采用丙烯酸化学接枝法对聚丙烯纤维进行表面改性,研究了改性聚丙烯纤维对发泡水泥塑性收缩开裂、力学性能及泡孔结构的影响.结果表明,改性聚丙烯纤维可改善发泡水泥的泡孔结构,并降低其塑性收缩开裂、细化其塑性收缩裂缝,同时可提高其抗折、抗压强度及弯曲韧性.纤维与水泥的质量比为0.7％时,试样的泡孔结构明显改善,塑性收缩开裂值下降了85.4％,且缝宽小于1 mm的塑性收缩裂缝比例高达73.1％,同时试样抗折及抗压强度分别增加48.8％和30.3％,弯曲韧性显著增加.利用傅里叶变换红外光谱仪、SEM、光学显微镜对改性前后聚丙烯纤维表面基团及发泡水泥试样的断面微观形貌、泡孔结构进行了分析,探讨了改性聚丙烯纤维的作用机制.
参考文献
| [1] | 邢锋,冷发光,冯乃谦,等.克裂速纤维增强混凝土抗裂性能[J].复合材料学报,2002,19(6):120-124.Xing Feng,Leng Faguang,Feng Naiqian,et al.Properties of cracking resistance of cemfiber reinforced concrete[J].Acta Materiae Compositae Sinica,2002,19(6):120-124. |
| [2] | 俞家欢,刘琼阳.水泥基复合材料中纤维拉拔的变位约束细观力学模型[J].复合材料学报,2008,25(5):147-150.Yu Jiahuan,Liu Qiongyang.Meso-scale variable engagement model for single fiber reinforced concrete under uniaxial tension[J].Acta Materiae Compositae Sinica,2008,25(5):147-150. |
| [3] | Uyama Y,Kato K,Ikada Y.Surface modification of polymers by grafting[J].Advances in Polymer Science,1998,137:1-39. |
| [4] | Buchenska J.Polypropylene fibers grafted with poly(acrylic acid)[J].Journal of Applied Polymer Science,2002,83(11):2295-2299. |
| [5] | Wang W,Wang L,Chen X,et al.Study on the graft reaction of poly(propylene) fiber with acrylic acid[J].Macromolecular Materials and Engineering,2006,291(2):173-180. |
| [6] | Kraai P P.A proposed test to determine the cracking potential due to drying shrinkage of concrete[J].Concrete Construction,1985,30(9):775-778. |
| [7] | Soroushian P,Mirza F,Alzozaimy A.Plastic shrinkage cracking of polypropylene fiber reinforced concrete[J].ACI Material Journal,1993,92(5):553-560. |
| [8] | 田 颖.芳纶纤维/水泥复合材料性能研究[D].济南:济南大学,2011.Tian Ying.Study on the properties of kelvar fiber/cement composite material[D].Jinan:University of Jinan,2011. |
| [9] | 全国水泥标准化技术委员会.GB/T 17671-1999水泥胶砂强度检验方法(ISO法)[S].北京:中国标准出版社,1998.National Technical Committee on Cement of Standardization Administration of China.GB/T 17671-1999.Method of testing cements-Determination of strength[S].Beijing:Standards Press of China,1988. |
| [10] | 沈荣熹,王璋水,崔玉忠.纤维增强水泥与纤维增强混凝土[M].北京:化学工业出版社,2006:23-30.Shen Rongxi,Wang Zhangshui,Cui Yuzhong.Fiber reinforced concrete[M].Beijing:Chemical Industry Press,2006:23-30. |
| [11] | Rengarayan R,Parameswaran V R,Lee S,et al.N.M.R.analysis of polypropylene-maleic anhydride copolymer[J].Polymer,1990,31(9):1703-1706. |
| [12] | Soroushian P,Ravanbakhsh S.Control of plastic shrinkage cracking with specialty cellulose fibers[J].ACI Materials Journal,1998,95(4):429-435. |
| [13] | 李秋义,张东兴,袁 杰.FRP复合理论与FRC复合理论[J].哈尔滨建筑大学学报,2002,35(3):74-78.Li Qiuyi,Zhang Dongxing,Yuan Jie.Composite theory of FRP and FRC[J].Journal of Harbin University of C E & Architecture,2002,35(3):74-78. |
| [14] | Romualdi J P,Mandel J A.Tensile strength of concrete affected by uniformaly distributed and closely spaced short lengths of wire reinforcement[J].ACI J Proc,1964,61(6):657-670. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%