探讨Nb2O5掺杂对Pb1-xLax(ZryTi1-y)1-x4O3(x=7%,0＜y＜1)(简称PLZT)压电陶瓷性能影响.通过X射线衍射及扫描电镜分析Pb1-xLax(ZryTi1-=y)1-x/4O3+0.5%NbzOs陶瓷的相组成和显微结构.结果表明:合成温度1060℃时,可以得到钙钛矿结构.随着Nb2O5掺杂量的增大,四方相的含量减少,准同型相界向三方相移动.掺杂NbzO5的质量分数为0.5%,Zr/Ti=57.5/42.5时,得到的压电陶瓷介电、压电性能最优,εT33/ε0=3100,tan6=1.96%,d33=550PC/N,Kp=0.67.