采用FT-IR、DSC等方法研究了亚甲基双邻氟苯胺(MOCA)/环氧树脂体系的固化行为,并对其固化动力学行为进行了研究.结果表明,体系固化行为与固化温度、固化时问及固化剂的用量有密切关系.其中固化剂的用量以MOCA质量分数在26%～33%为宜.当MOCA含量在28.6%时,最佳固化条件为:由最佳起始固化温度165℃左右缓慢升温到208℃左右恒温固化,最后在258℃左右恒温一段时间使树脂充分固化.其固化反应方程为:-dα/dt=k(1-α)1.15.
参考文献
| [1] | 姚燕,孟祥玲.环氧树脂用固化剂的研究进展[J].现代涂料与涂装,2007(04):37-40. |
| [2] | Maity T;Samanta BC;Dalai S;Banthia AK .Curing study of epoxy resin by new aromatic amine functional curing agents along with mechanical and thermal evaluation[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2007(1-2):38-46. |
| [3] | Pellegrino Musto;Mario Abbate;Giuseppe Ragosta .A study by Raman,near-infrared and dynamic-mechanical spectroscopies on the curing behaviour,molecular structure and viscoelastic properties of epoxy/anhydride networks[J].Polymer: The International Journal for the Science and Technology of Polymers,2007(13):3703-3716. |
| [4] | 韦春,钟文斌,刘敏娜,王霞瑜.环氧树脂/液晶固化剂固化反应动力学研究[J].热固性树脂,2002(02):15-18. |
| [5] | 易长海,李娟,甘厚磊.水性环氧树脂固化反应的研究[J].粘接,2007(01):11-13. |
| [6] | 易长海,尹业高,李建宗,程时远.环氧树脂潜伏性体系固化反应动力学研究[J].热固性树脂,2000(01):13-15. |
| [7] | 袁骏.红外光谱分析在环氧树脂与胺固化剂反应中的一些简单应用[J].上海涂料,2003(02):30-34. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%