采用室温固相复合技术制备AgCuIn/QSn复合焊料，选用不同退火温度对AgCuIn/QSn复合焊料进行扩散退火，利用拉力试验机、扫描电子显微镜考察热处理温度对AgCuIn/QSn复合焊料界面的影响。结果表明，退火工艺为550℃/6 h时复合界面结合效果最佳。
The AgCuIn/QSn composite brazing was made by room temperature solid phase composite technology, and annealed at different heat treatment temperatures. The influence of annealing temperature on the AgCuIn/QSn composite brazing composite interface was studied by tensile testing instrument and scanning electron microscopy. The results showed that the best composite interface was got at 550℃/ 6 h annealing.