利用低温液氮球磨技术制备了Sm-Fe合金粉体,采用XRD、HRTEM和惰性气脉冲-红外-热导等方法对Sm2Fe17合金粉体在液氮球磨过程中的组织演变进行了研究.结果表明,液氮球磨可加速细化Sm-Fe合金粉体.球磨5 h后,Sm-Fe合金的晶粒尺寸约为10 nm,9 h后晶粒尺寸约为5 nm.Sm-Fe合金中的氮含量随着球磨时间的延长而增加,主轴转速150 r/min球磨9 h后,氮含量达1.62%(质量分数,下同).随着球磨时间的延长,Sm2Fe17相向非晶态转变,降低球磨转速可以延缓非晶的形成过程.
参考文献
| [1] | Suryanarayana C. .Mechanical alloying and milling [Review][J].Progress in materials science,2001(1/2):1-184. |
| [2] | Xu J;He J H;Ma E .[J].Metallurgical and Materials Transactions,1997,A28(07):1569. |
| [3] | Perez R J;Huang B;Lavernia E J .[J].Nano-Structured Materials,1996,7(05):565. |
| [4] | Zhang X;Wang H;Narayan J et al.[J].Acta Materialia,2001,49:1319. |
| [5] | Pinga D H;Honoa K;Hidaka T .[J].Journal of Magnetism and Magnetic Materials,2004,277(03):337. |
| [6] | YANG Bin,FAN Jianzhong,HAO Bin,TIAN Xiaofeng,CHENG Junsheng,ZHANG Jishan.Synthesis and characterization of nanocrystalline Ni produced by cryomilling in liquid nitrogen[J].稀有金属（英文版）,2007(02):147-151. |
| [7] | 杨滨,程军胜,樊建中,田晓风,陈汉宾,张济山.低温球磨纳米晶Al-Zn-Mg-CU合金组织的演变[J].金属学报,2005(11):1195-1198. |
| [8] | Ding J;Mccormick P G;Street R .[J].Applied Physics Letters,1992,61(22):2721. |
| [9] | 陈振华;陈鼎.机械合金化与固液反应球磨[M].北京:化学工业出版社,2006:298. |
| [10] | 肖军,潘晶,刘新才.高能球磨法及其在纳米晶磁性材料制备中的应用（一）[J].磁性材料及器件,2005(01):6-10. |
| [11] | 孙继兵,崔春翔,吴瑞国,杨伟,刘玉岭.Sm12.8Fe87.2合金氮化前后高能球磨的研究[J].兵器材料科学与工程,2005(06):5-9. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%