Nb-Ti hot-rolled TRIP-assisted steel with high plasticity and appropriate volume percentage of retained austenite based on fine ferrite grain have been developed in the experiment. The test results showed that niobium tend to exist in solution state in matrix with less precipitation, and niobium-titanium could be precipitated in form of (Nb, Ti)C or (Nb, Ti) (C, N), which play an important role in increasing yield strength (from 495 MPa to 610 MPa). Besides, the retained austenite had a positive effect on improving the plasticity by transformation into martensite during tensile deformation.
参考文献
| [1] | J Elfmark .[J].Journal of Steel Related Mater,2003,4:299. |
| [2] | Y Sakuma;D K Matlock;G Krauss .[J].Metallurgical and Materials Transactions,1992,23A:1221. |
| [3] | K Sugimoto;N Usui;M Kobayashi;S Hashimoto .[J].ISIJ International,1992,32:1311. |
| [4] | Y.Chen,G.Y.Tang,W.Liu,Q.Liu,P.H.Li,X.Chen.THE CHARACTERISTICS OF MICROSTRUCTURES AND PROPERTIES FOR ADVANCED ALUMINUM/SILICON CONTAINED HOT-ROLLED TRIP STEELS[J].金属学报（英文版）,2004(06):823-829. |
| [5] | S C Balk;S Kim;Y S Jin .[J].ISIJ International,2001,41(03):290. |
| [6] | V F Zackay;E R Parker;D Fahr;R Ruch .[J].Transactions of ASM Quarter,1967,60:252. |
| [7] | G R Chanani;V F Zackay;E R Picker .[J].Metallurgical and Materials Transactions,1971,2:133. |
| [8] | W. Bleck;J. Ohiert .Sheet metal forming behaviour and mechanical properties of TRIP steels[J].Steel Research,1999(11):472-479. |
| [9] | N Mizui .[J].CAMP-ISIJ,1992,5:837. |
| [10] | Y.Chen,X.Chen,P.H.Li,S.K.Pu,Z.X.Yuan,B.F.Xu,D.X.Lou,A.M.Guo,S.B.Zhou.EFFECT OF CARBON CONTENT ON MICROSTRUCTURE AND PROPERTIES OF HIGH STRENGTH AND HIGH ELONGATION STEELS[J].金属学报(英文版),2003(01):65-71. |
| [11] | G U Bohm .[J].Steel Grips,2003,4:305. |
| [12] | C G Lee;S J Kim;C S Oh;S H Lee .[J].ISIJ International,2002,42(10):1162. |
| [13] | Patrick Van Hecke;Jan Penning .[J].Steel Grips,2003,4:273. |
| [14] | Y Sakuma;O Matsumura;H Takechi .[J].Metallurgical and Materials Transactions,1991,22A:489. |
| [15] | Y.Chen,X.Chen,A.M.Guo,D.X.Luo,B.F.Xu,Z.X.Yuan,P.H.Li,S.K.Pu,S.B.Zhou.RESEARCH ON CHEMICAL COMPOSITION AND MICROSTRUCTURE OF NEWLY-DEVELOPED HIGH STRENGTH AND HIGH ELONGATION STEELS[J].金属学报(英文版),2003(02):122-131. |
| [16] | Y.Chen,X.Chen,Z.X.Yuan,B.F.Xu,A.M.Guo,P.H.Li,S.K.Pu.EFFECTS OF CARBON CONTENT AND ROLLING PROCESSING ON RETAINED AUSTENITE FOR HOT-ROLLED TRIP STEELS[J].金属学报(英文版),2002(05):439-447. |
| [17] | Y.Chen,X.Chen,Q.F.Wang,G.L.Yuan,C.Y.Li,X.Y.Li,Y.X.Wang.EFFECT OF CHEMICAL COMPOSITION ON RETAINED AUSTENITE IN TRIP STEEL[J].金属学报(英文版),2002(04):339-345. |
| [18] | Yu CHEN,Guoyi TANG,Fangyu CHEN,Pinghe LI,Sunbing ZHOU.Research on Retained Austenite for Advanced Aluminum-containing Hot-rolled TRIP Steel[J].材料科学技术学报（英文版）,2005(06):813-816. |
| [19] | Yu CHEN,Guoyi TANG,Feipeng LI,Yu ZHANG,Xiao CHEN,Pinghe LI,Wei LIU,Qing LIU.Microstructure Features with Ultrafined and Purified Grains for Si-Mn Hot-rolling TRIP Steel[J].材料科学技术学报（英文版）,2005(06):799-802. |
| [20] | GB 8362-1987.GB 8362-1987.Quantitative Determination Method of X-ray Diffractometer[S].,1987. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%