Variations of Microstructure and Mechanical Properties of Si-B-O-N Ceramics with Sintering Temperatures

材料科学技术（英文）, 2002, 18(4): 343-346.

^1, , ^2, , ^3, , ^4, , ^5,

1.School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China

2.School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China

3.School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China

4.School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China

5.School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China

基金项目: 国家自然科学基金(50072002)

Variations of Microstructure and Mechanical Properties of Si-B-O-N Ceramics with Sintering Temperatures

Keywords： Si-B-O-N ceramics

Si-B-O-N powder without B-O bonds synthesized by polymeric precursor were hot-pressed into ceramics at different temperatures. The variations of microstructure and mechanical properties of Si-B-O-N ceramics have been investigated. Crystallization of Si-B-O-N ceramics occurred at about 1400°C. Density, elastic modulus, and flexural strength of the ceramics increased with the increasing sintering temperatures, and reached to their maximum values at 1600°C. By contrast, hardness and fracture toughness of the ceramics monotonically changed with increasing sintering temperatures. Hardness decreased, while the fracture toughness increased. The principal toughening mechanisms including crack deflection, crack bridging and plate grain pulling-out effects are discussed

参考文献

[1]	R T Paine;C K Narula .[J].Chemical Reviews,1990,90:90,73.
[2]	T Wideman;E E Remsen;E Cortez;V L Chl,a ,L G Sneddon.[J].CHEMISTRY OF MATERIALS,1998(10):10,412.
[3]	L Bois p L′Haridon;Y Laurent;X Gouin P;Grange,J F Letard , M Birot.[J].Journal of Alloys and Compounds,1996:232,244.
[4]	O Funayama;H Nakahara;A Tezuka;T Ishii ,T Isoda .[J].Journal of Materials Science,1994,29:2238.
[5]	O Funayama;H Nakahara;M Okoda;M Okumura,T Isoda .[J].Journal of Materials Science,1995,30:410.
[6]	M Maeda .[J].Japanese Journal of Applied Physics,1990,29:1789.
[7]	Junbao ZHANG,Tingquan LEI,Guangwu WEN,Yu ZHOU.Synthesis and Ceramic Conversion of Polysiloxazane to Silicon Oxynitride[J].材料科学技术学报(英文版),2001(01):3-4.
[8]	J B Zhang;G W Wen;T Q Lei.[J].Journal of Materials Science Letters
[9]	G Wen;G L Wu;T Q Lei;Y Zhou,Z X Guo .[J].Journal of the European Ceramic Society,2000,20:1923.
[10]	M B Fegley.[J].Communication of the American Ceramic Society,1981:9,235.
[11]	Guilin WU;Master D .[D].Thesis, Harbin Institute of Technology,1999.
[12]	D Barukm;S P Tremblay;M Fiset .[J].Journal of Materials Science,1993,28:5486.
[13]	C Kaya;F Kaya;P A Trusty;A R Boccaccini ,M MarsogluCeram .[J].Inter,1999,25:359.
[14]	C Kaya;F Kaya;M Marsoglu .[J].MSE,1998,A247:75.
[15]	M. Poorteman;P. Descamps .Anisotropic Properties in Hot Pressed Silicon Nitride—Silicon Carbide Platelet Reinforced Composites[J].Journal of the European Ceramic Society,1999(13/14):2375-2380.

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

Variations of Microstructure and Mechanical Properties of Si-B-O-N Ceramics with Sintering Temperatures

参考文献