用溶胶-凝胶法制备了Sm2-xCexCuO4(SCC,x=0,0.1,0.2,0.3)粉体,干压成片状并烧结为陶瓷,采用XRD、SEM等对SCC粉体和陶瓷片的物象、形貌进行了表征.以SCC陶瓷片为阴极、Nafion膜为质子导体、Nj-Ce0.8Sm0.2:O2-δ(Ni-SDC)陶瓷片为阳极,银-铂网为集流体组成单电池,以湿氢气和氮气为原料,在298～373 K温度范围内研究了SCC在电化学合成氨中的性能.结果表明在研究的温度范围内和施加电压条件下,使用SCC为阴极均有氨气生成,其中Sm1.8Ce0.2CuO4电化学合成氨速率最高,在353 K时合成氨速率为1.05×10-8mol·s-1·cm-2.
参考文献
| [1] | Marnellos G;Stoukides M .Ammonia synthesis at atmospheric pressure[J].Science,1998,282(5386):1-8. |
| [2] | Li ZJ;Liu RQ;Wang JD;Xie YH;Yue F .Preparation of BaCe0.8Gd0.2O3-delta by the citrate method and its application in the synthesis of ammonia at atmospheric pressure[J].Journal of solid state electrochemistry,2005(4):201-204. |
| [3] | Ji-De Wang;Ya-Hong Xie;Zheng-Fang Zhang;Rui-Quan Liu;Zhi-Jie Li .Protonic conduction in Ca~(2+)-doped La_2M_2O_7 (M = Ce, Zr) with its application to ammonia synthesis electrochemically[J].Materials Research Bulletin: An International Journal Reporting Research on Crystal Growth and Materials Preparation and Characterization,2005(8):1294-1302. |
| [4] | Liu RQ;Xie YH;Wang JD;Li ZJ;Wang BH .Synthesis of ammonia at atmospheric pressure with Ce0.8M0.2O2-delta (M=La, Y, Gd, Sm) and their proton conduction at intermediate temperature[J].Solid state ionics,2006(1/2):73-76. |
| [5] | 王进,刘瑞泉,王吉德,刘玉星.磺化聚砜质子交换膜在低温常压电化学合成氨中的应用[J].科学通报,2008(09):1032-1035. |
| [6] | 王进,刘瑞泉.SDC和SSC在低温常压电化学合成氨中的性能研究[J].化学学报,2008(07):717-721. |
| [7] | 孙凡,刘瑞泉,王吉德,郝家勇,丁琳.天然气燃料电池中双层阳极Ni-SDC的性能[J].电源技术,2007(06):462-464. |
| [8] | 史雅珍;熊新向;谌翔希 .奈氏试剂与铵离子的显色应及光度法定氮[J].武汉冶金科技大学学报(自然科学版),1998,21(01):40-43. |
| [9] | 孙丽萍,霍丽华,赵辉,Christophe Pijolat.中温固体氧化物燃料电池阴极材料Sm2-xCexCuO4的制备与性能研究[J].无机化学学报,2007(09):1545-1549. |
| [10] | 陈羚,程璇,张颖,刘晶,范钦柏.质子交换膜Nafion（R）的导电性与物理老化[J].高分子材料科学与工程,2005(05):181-184. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%