The effects of oxygen on the microstructure of Ti-47Al-0.7B (at. pct) alloy for as-cast automotive valves were investigated. Six alloys with oxygen content from 0.4 to 1.4 at. pct were prepared by induction melting and centrifugal casting in CaO crucible under protective atmosphere. The microstructures were observed by optical microscopy (OM) and scanning electron microscope (SEM). The results show that the increase of oxygen content led to grain refinement and enhanced the microhardness as well as the α2 volume fraction in the TiAl-based alloys.
参考文献
| [1] | |
| [2] | Y.W. Kim and D.M. Dimiduk: JOM, 1991, 43, 40.[2]Y.W. Kim: JOM, 1994, 46, 30.[3]Y.W. Kim and D.M. Dimiduk: Structural Intermetallics 1997, eds. M.V. Nathal, R. Darlia, C.T. Liu, P.L. Martin, D.B. Miracle, R. Wagner and M. Yamaguchi, TMS, Warrendale, PA, 1997, 531.[4] M. Yamaguchi, H. Inui and K. Ito: Acta Mater, 2000, 48, 307. [5]M. Lamirand, J.L. Bonnentien and J.P. Chevalier: Structural Intermetallics 2003, eds. Y.M. Kim, H. Clemens and A.H. Rosemberger, TMS, Warrendale, PA, 2003, 97.[6] K. Liu, Y.C. Ma, M. Gao, G.B. Rao, Y.Y. Li, W. Ke, X.H. Wu and M.H. Loretto: Intermetallics, 2005, 13, 925.[7]ASTM E112-96: Standard Test Methods for Determining Average Grain Size, American Society for Testing and Materials, Conshohocken, PA, 2004.[8] Y. Jin, J.N. Wang, J. Yang and Y. Wang: Scripta Mater, 2004, 51, 113.[9] T.T. Cheng: Intermetallics, 2000, 8, 29.[10]W. Lefebvre, A. Loiseau and A. Menand: Structural Intermetallics 2003, eds. Y.M. Kim, H. Clemens and A.H. Rosemberger, TMS, Warrendale, PA, 2003, 65.[11]W. Lefebvre, A. Loiseau, M. Thomas and A. Menand: Philos. Mag. A, 2002, 82, 2341.[12]G.B. Rao, K. Liu, E.H. Han and W. Ke: Chin. J. Nonferrous Met., 2004, 14(S1), 265. (in Chinese)[13] S. Tamirisakadala, R.B. Bhat, J.S. Tiley and D.B. Miracle: Scripta Mater, 2005, 53, 1421.[14] D. Hu: Intermetallics, 2001, 9, 1037.[15] M.D. Graef, J.P.A. Lofvander, C. McCullough and C.G. Levi: Acta Metall. Mater, 1992, 40, 3395.[16] M.E. Hyman, C. McCullough, J.J. Valencia, C.G. Levi and R. Mehrabian: Metall. Trans. A, 1991, 22, 1647.[17] J. Zollinger, J. Lapin, D. Daloz and H. Combeau: Intermetallics, 2007, 15, 1343. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%