The 1Cr18Ni9Ti specimens were treated respectively with pulse current under 520 V and 2 600 V during solidification and the solidification structure was observed. The results showed that pulse current can refine solidification grains, cut primary dentrities remarkably and reduce second dentritic arm spacing. The mechanism and effect are changed with operation parameters.
参考文献
| [1] | Nakada M;Shiohara Y;Flemings M C .Modification of Solidi-fication Structures by Pulse Electric Discharging[J].ISIJ International,1990,30(01):27-33. |
| [2] | Barnak J P;Sprecher A F;Conrad H .Colony (Grain) Size Re-duction in Eutectic Pb-Sn Castings by Electroplusing[J].Scripta Metallurgica et Materialia,1995,32(06):879-884. |
| [3] | Yan Hong-chun;He Guan-hu;Zhou Ben-lian et al.The In-fluence of Pulse Electric Discharging on Solidified Structure ofSn-10 %Pb Alloy[J].Acta Metallurgica Sinica,1997,33(04):352-358. |
| [4] | WANG Jian·zhong .The Research of Treating Technology withElectro-Pulse Modification and the Hypothesis of Liquid MetalCluster Structure[D].Beijing: University of Science andTechnology Beijing,1998. |
| [5] | 訾炳涛,崔建忠,巴启先.高密度脉冲电流作用下LY12铝合金的凝固组织[J].特种铸造及有色合金,2000(04):4-6. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%