选用合金Inconel 690和693作为研究对象,着重研究了它们在铁磷酸盐玻璃熔体中的腐蚀行为.分别计算了不同电极材料的尺寸损失和质量损失,以及相应的损失速率,采用SEM,EDS和XRD等手段对材料表面的腐蚀层进行了分析,确定了腐蚀层的成分,主要相组成及其晶粒形态,讨论了材料腐蚀发生的可能机理.结果表明,在玻璃熔体内,合金Inconel 693比Inconel 690更耐腐蚀.随着腐蚀时间的延长,合金的腐蚀速率都逐渐降低.合金试样表面的腐蚀层主要由固熔体(Fe,Cr)2O3组成.
参考文献
| [1] | Lambert S L;Kim D S .Tank Wast Rem PNNL #WHC-SP-1143[R].Hanford:PNNL,1994. |
| [2] | Perez J M;Bickford D F;Day D E et al.PNNL-13582[R].Hanford:PNNL,2001. |
| [3] | Day D E;Wu Z et al.[J].Journal of Non-Crystalline Solids,1998,241(01) |
| [4] | DOE U S .Summary Data on the Radioactive Waste,Spent Nuclear Fuel,and Contaminated Media Managed by the US Department of Energy[R].US Washington D C:Department of Energy,2001. |
| [5] | Kim C W;Zhu D;Day D E et al.[J].British Ceramic Transactions,2003,143:329. |
| [6] | 赵宏生,李艳青,周万城,罗发,唐春和.MoO3-V2O5-P2O5-Fe2O3玻璃的制备及性能研究[J].无机材料学报,2005(03):563-569. |
| [7] | Zhu Dongmei;Zhou Wancheng;Zhao Hongsheng .[J].Journal of Non-Crystalline Solids,2001,279(2-3):204. |
| [8] | Leerssen R D .Iron Phosphate Glass for the Vitrification of INEEL Sodium Bearing Waste and Hanford Low Activity Waste[D].Rolla:University of Missouri-Rolla,2002. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%