A new plastic deformation process for gray cast iron named cylinder covered compression (CCC) was developed. By CCC process, gray cast iron (GCI) specimens, which are embedded in steel cylinders, were hot compressed up to 80% reduction in height without the cracking problem. It was clearly observed that the uniform distribution of directional graphite flakes appeared after more than 45% reduction hot compression. The strength, ductility, and microhardness of GCI after 80% reduction deformation were significantly enhanced: the tensile strength varied from 117 MPa to 249 MPa, while the total elongation varied from 0 to 5.2%, and the microhardness varied from 153 HV to 217 HV. It was shown that the tensile fracture surface presented ductility characters after more than 45% reduction hot deformation.
参考文献
| [1] | HE Z R;LIN G X;JI S .Deformation and Fracture of Cast Iron With an Optimized Structure[J].Materials Characterization,1997,38:251-258. |
| [2] | ZHANG Y;CHEN Y;HE R et al.Investigation of Tribological Properties of Brake Shoe Materials-Phosphorous Cast Irons With Different Graphite Morphologies[J].Wear,1993,166:179-186. |
| [3] | A. R. Ghaderi;M. Nili Ahmadabadi;H. M. Ghasemi .Effect of graphite morphologies on the tribological behavior of austempered cast iron[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2003(1/6):410-416. |
| [4] | JIANG Jian-qing;SHU Guang-ji .Structure and Properties of Unidirectionally Solidified Fe-C-Si Eutectic Alloy (in Chinese)[J].Journal of Iron and Steel Research,1997,32(05):53-59. |
| [5] | ZHAO X;JING T F;GAO Y W et al.A New SPD Process for Spheroidal Cast Iron[J].Materials Letters,2004,58:2335-2339. |
| [6] | 初瑞清,段占强,董翰,杨柯,李守新,王中光.微型拉伸试样的设计及其在高性能管线钢研究中的应用[J].金属学报,2000(06):626-629. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%