利用电化学阻抗谱(EIS)研究B95铝合金在添加H2O2的0.01 mol/L CeC13溶液中铈盐转化膜的形成过程,以及H202对合金表面成膜过程的影响.结果表明,EIS的变化清楚显示了B95铝合金在CeC13溶液中的成膜过程.转化膜的成膜过程可以分成三个阶段:形成阶段,成长阶段和稳定平衡阶段.在0.01 mol/LCeCl3溶液中浸泡生成的转化膜不够致密,随着在溶液中浸泡时间的延长,转化膜的性能下降;添加H2O2后,一方面加快铈盐转化膜形成速度,特别是形成阶段,使原需24 h的过程缩短为1.5 h;另一方面,H2O2促使B95表面转化膜更加致密,阻止水的渗透,转化膜的阻抗值呈现逐渐增大的趋势.
参考文献
| [1] | Hinton B R W.The inhibition of aluminum corrosion by cerium cations[J].Mater.Forum,1984,7(4):211. |
| [2] | Hinton B R W.The inhibition of aluminum alloy corrosion by rare earth metal cations[J].Corros.Australia,1985,210(3):12. |
| [3] | Arnott D R.Cationic film forming inhibitors for the protection of AA7075 aluminum alloy against corrosion in aqueous chloride solution[J].Corrosion,1989,45(1):12. |
| [4] | Mansfeld F,Lin S,Kim S,et al.Surface modification of Al alloys and Al-based metal-matrix composites by chemical passivation[J].Electrochem.Acta,1989,34(8):1123. |
| [5] | Arnott D R.Auger and XPS studies of cerium corrosion inhibition on 7075 aluminum alloy[J].Appl.Surf.Sci.,1985,22/23:236. |
| [6] | Hinton B R W.Corrosion Inhibition with rare earth metal salts[J].J.Alloy Compd.,1992,180:15. |
| [7] | Hinton B R W,Arnott D R,Ryan N E.Cerium conversion coating for the corrosion protection of aluminum[J].Mater.Forum,1986,9(3):162 |
| [8] | 顾宝珊,刘建华,纪晓春.铈盐对铝合金的缓蚀机理研究[J].中国腐蚀与防护学报,2006,26(1):53. |
| [9] | Gu B S,Liu J H.Corrosion inhibition mechanism of rare earth metal(REM) on LC4 Al alloy with the spilt cell technique[J].J.Rare Earths,2006,24(1):89. |
| [10] | 王新东,吴世民,刘艳芳等.用电化学交流阻抗法研究铝合金表面稀t转化膜[J].北京科技大学学报,2001,23 (4):320. |
| [11] | 曹楚南,张鉴清.电化学阻抗谱导论[M].北京:科学出版社,2002:81. |
| [12] | 顾宝珊,刘建华.铈盐对铝合金的成膜过程电化学交流阻抗研究[J].中国稀土学报,2007,25(2):210. |
| [13] | 顾宝珊,刘建华.铝合金表面稀土转化膜性能与耐蚀机理研究[D].北京:北京航空航天大学,2007:47. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%