通过对Al-Ga-Sn-Mn-Bi阳极合金进行480℃的固溶和退火处理,研究不同热处理方式对合金的组织及电化学性能的影响.结果表明,固溶处理使阳极合金中的析出相数量减少,合金的耐蚀性得到提高,恒流放电电位负移且放电平稳;退火处理后,析出相均匀度及数量增加,耐蚀性降低,恒流放电曲线平稳.通过性能对比发现,固溶处理效果优于退火处理.
参考文献
| [1] | 王兆文,李延祥,李庆峰,高炳亮,邱竹贤.铝电池阳极材料的开发与应用[J].有色金属,2002(01):19-22. |
| [2] | Eishaye H A;Abd E I;Wahab F M .Effect of gallingions on the electrochemical behavior of Al,A1-Sn,Al-Zn and Al-Zn-Sn alloys in chloride solutions[J].Corrosion Science,2001,43(04):643-654. |
| [3] | Gurrappa I .The surface free energy and anode efficiency of aluminum alloys[J].Corrosion Prevention & Control,1993,40(04):111-114. |
| [4] | 贺俊光,文九巴,李旭东,郝庆国.热处理对Al-Zn-Sn-Ga-Mg合金组织和电化学性能的影响[J].材料热处理学报,2011(07):110-115. |
| [5] | Ponchel B M;Hosrst R L .Performance of Al-Zn-Sn alloy anodes in sea water service[J].Materials Protection,1968,7(03):38-41. |
| [6] | Lennox T J;Peterson M H;Groover R E .A study of electrochemical efficiencies of aluminum galvanic anodes in sea water[J].Materials Protection,1968,7(02):33-37. |
| [7] | Lin J C;Shth H C .Improvement of the current efficiency of an Al-Zn-In anode by heat-treatment[J].Eletrochemical Society,1987,134(04):817-823. |
| [8] | 马景灵,文九巴,李旭东,李光福,焦孟旺,郭炜.热处理对Al-Zn-In-Mg-Ti合金组织与电化学性能的影响[J].材料热处理学报,2008(03):113-117. |
| [9] | 郝小军,宋诗哲.铝锌合金在3%NaCl溶液中的电化学行为[J].中国腐蚀与防护学报,2005(04):213-217. |
| [10] | 丁振斌,朱梅五,孔小东.铝合金阳极微观组织对其性能的影响[J].材料保护,2002(07):8-10. |
| [11] | 马力,李威力,曾红杰,闫永贵,侯保荣.低驱动电位Al-Ga合金牺牲阳极及其活化机制[J].中国腐蚀与防护学报,2010(04):329-332. |
| [12] | 曹楚南;张鉴清.电化学阻抗谱导论[M].北京:科学出版社,2002 |
| [13] | 邵海波,王建明,王晓艳,郑奕,张鉴清.纯铝在KOH-乙醇溶液中的电化学行为[J].电化学,2004(04):430-434. |
| [14] | 贺俊光,文九巴,李旭东,郝庆国.Al-Zn-Sn-Ga阳极腐蚀过程的电化学阻抗谱[J].中国有色金属学报,2012(01):187-193. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%