The Li1.02NbxMn2-xO4 (x=0, 0.005, 0.01, 0.0:2, 0.04 and 0.1) materials were prepared by solid-state reaction method in which Li2CO3, electrolytic MnO2 and Nb2O5 were used as reactants. The influences of the Nb5+ doping on structure, morphology and electrochemical performance were systemically investigated by means of X-ray diffraction (XRD), scanning electron microscopy (SEM), cyclic voltammetry (CV) and AC impedance. XRD test showed that the prepared samples had single spinel structure although there was impurity phase of LiNbO3 existing in Li1.02NbxMn2-xO4 phase after Nb5+ doping. The doped materials with Nb5+ had smaller lattice parameters and crystal volume compared with pristine Li1.02Mn2O4. The endurance of overcharge was largely improved. In addition, the small amount of Nb5+ doping could increase the material conductivity.
参考文献
| [1] | D. Arumugam;G. Paruthimal Kalaignan .Electrochemical characterizations of surface modified LiMn_2O_4 cathode materials for high temperature lithium battery applications[J].Thin Solid Films,2011(1):338-343. |
| [2] | D. Arumugam;G. Paruthimal Kalaignan .Synthesis and electrochemical characterizations of nano-La_2O_3-coated nanostructure LiMn_2O_4 cathode materials for rechargeable lithium batteries[J].Materials Research Bulletin: An International Journal Reporting Research on Crystal Growth and Materials Preparation and Characterization,2010(12):1825-1831. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%