在氧化钇含量为8%(摩尔分数)的氧化锆中加入单斜氧化锆,1600℃常压烧结,制得不同含量的氧化钇稳定氧化锆.研究了不同含量的氧化钇对氧化锆陶瓷性能的影响,并对相组成及显微结构进行了分析.当氧化钇的摩尔分数为3%时,材料的相对密度、抗弯强度、硬度等综合力学性能同时达到最大值.超过这个临界点,材料力学性能又会逐渐下降.
With adding m-ZrO2 to zirconia with 8mol% yttria,stabilized zirconia is prepared by sintering at 1600℃.The effect of the content of yttria on the mechanical properties of zirconia ceramic and the phase as well as microstructure of zirconia ceramic with different molar fraction yttria are studied.The results show that the best mechanical properties of ZrO2 stabilized by Y2O3 can be obtained when Y2O3 content is 3mol%.Over the critical content,the mechanical properties of zirconia ceramic gradually decrease.
参考文献
| [1] | 周泽华,丁培道,陈蓓,易于.相含量的变化对氧化锆陶瓷性能的影响[J].材料热处理学报,2002(01):43-45. |
| [2] | 李杰,唐子龙,张中太.微量掺杂对 8%Mg-部分稳定氧化锆晶粒尺寸和相组成的影响[J].硅酸盐学报,2003(01):25-30. |
| [3] | Garive R C;Nelson P S .Phase analysis in zirconia systerm[J].Journal of the American Ceramic Society,1972,55(06):303. |
| [4] | 孟国文;陈大明;康沫狂 等.Y2O3含量及制备工艺参数对Y-TZP纳米粉烧结体性能的影响[J].功能材料,1996,27(01):92. |
| [5] | 周泽华,丁培道,陈蓓,易于.氧化锆力学性能和热学性能的综合分析[J].重庆大学学报(自然科学版),2002(02):60-62. |
| [6] | 尹衍升;李嘉.氧化锆陶瓷及其复合材料[M].北京:化学工业出版社,2004:13. |
| [7] | 孙义海,张玉峰,郭景坤.添加剂对3Y-TZP材料烧结行为及力学性能的影响[J].硅酸盐学报,2002(05):569-573. |
| [8] | 饶平根,叶建东,岩佐美喜男,近藤功.低温烧结3Y-TZP陶瓷的力学性能和耐磨性能[J].华南理工大学学报(自然科学版),2001(11):62-66. |
| [9] | 张玉峰,郭景坤,黄校先,李包顺.添加剂对Y-TZP烧结及力学性能影响[J].硅酸盐学报,1998(03):373-377. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%