研究了车轮钢中白点形成的机理以及白点对断口形貌的影响.结果表明,氢和空位聚集导致鼓泡形核和长大,随着鼓泡内氢气压力的升高,裂纹从鼓泡核壁形核、扩展导致白点形成.白点的断口为准解理,和氢致滞后开裂断口相同,含白点试样的断口形貌依赖于断裂方式和试样厚度.钢中的白点除了产生二次裂纹和局部准解理断面外,对各种断口形貌均没有明显的影响.
参考文献
| [1] | Steiner J E.Current Solution to Hydrogen Problems in Steel[M].Ohio:ASM,1982 |
| [2] | R.J.Fruehan .A Review of Hydrogen Flaking and Its Prevention[J].Iron & Steelmaker,1997(8):61-69. |
| [3] | Wu Yang Chu;K.W. Gao;J. X. Li .Hydrogen blistering and hydrogen-induced fracture of rail steel[J].Steel Research,2001(2):66-69. |
| [4] | Pollard M G .Tyre Fracture:the Problem,the Cause and Preventative Action[J].Proceedings of the Institution of Mechanical Engineers,1999,213F:181-195. |
| [5] | Andrew J H;Lee H;Lloyd H K et al.Hydrogen Transformation Characteristics in Steel[J].Journal of Iron and Steel Institute,1947,156:208-224. |
| [6] | 陈廉;刘民治;尹万全 等.气瓶钢中白点焊合的研究[J].金属学报,1979,15(04):446-455. |
| [7] | R. B. McLellan;Z. R. Xu .HYDROGEN-INDUCED VACANCIES IN THE IRON LATTICE[J].Scripta materialia,1997(10):1201-1205. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%