采用MARC/Superform有限元软件对平面应变压缩过程进行了二维有限元分析,分析了上下模具尺寸不相等时,对金属流变规律及其力能参数的影响.同时应用滑移线场理论对端部的滑移线场进行了分析,分析了金属的流动情况,进一步验证了有限元模拟结果的可靠性.研究结果显示:模具尺寸相等时,金属流动呈现对称分布;当上下两个模具尺寸不等时,金属流动呈现非对称分布,有剪切变形产生.而且随着模具尺寸差的增大,其交叉剪切变形越严重,总压力也增大,平均压力相对降低,这与异步轧制过程类似.所研究结果为异步轧制过程提供了一种新的物理模拟方法.
参考文献
| [1] | R. J. Hand;S. R. Foster;C. M. Sellars .Temperature changes during hot plane strain compression testing[J].Materials Science and Technology: MST: A publication of the Institute of Metals,2000(4):442-450. |
| [2] | N. J. Silk;M. R. van der Winden .Interpretation of hot plane strain compression testing of aluminium specimens[J].Materials Science and Technology: MST: A publication of the Institute of Metals,1999(3):295-300. |
| [3] | M. S. Mirza;C. M. Sellars .Modelling the hot plane strain compression test Part 2 - Effect of friction and specimen geometry on spread[J].Materials Science and Technology: MST: A publication of the Institute of Metals,2001(9):1142-1148. |
| [4] | 吕爱强,蒋奇武,王福,左良,梁志德.异步轧制对高纯铝箔冷轧织构的影响[J].金属学报,2002(09):974-978. |
| [5] | 黄涛,曲家惠,胡卓超,王福,左良.高纯铝箔在异步轧制和再结晶过程中取向的演变[J].金属学报,2005(09):953-957. |
| [6] | 高秀华,齐克敏,邱春林.硅钢极薄带三次再结晶退火过程中的组织演化[J].材料热处理学报,2006(04):91-94. |
| [7] | Su-Hyeon Kim;Bong-Sim You;Chang Dong Yim .Texture and microstructure changes in asymmetrically hot rolled AZ31 magnesium alloy sheets[J].Materials Letters,2005(29/30):3876-3880. |
| [8] | 张文玉,刘先兰,陈振华,夏伟军.异步轧制对AZ31镁合金板材组织和性能的影响[J].武汉理工大学学报,2007(11):57-61. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%