Fe3O4 nanoparticles were prepared by chemistry co-precipitation and the mean crystal size was 17.9 nm measured by XRD. After it had been treated by silane-coupling agents KH570, magnetic micro-spheres dispersed in organic medium glycol were gained and the mean size of Fe3O4 nanopowders was 33.7 nm . So it can be concluded that magnetic micro-sphere is made of a few Fe3O4 crystals. Many factors of modification were researched, such as the time of ball milling, the content of Fe3O4 and the content of KH570. The modification of Fe3O4 is relative to the time of ball milling, but the dominant function is affected by the content of Fe3O4 and KH570. When the content of Fe3O4 is known, there is a suitable content of KH570. Different content of Fe3O4 will make the different suitable content of KH570, but the range of latter is less than former, which is relative to the distribution of KH570 on Fe3O4 surface or in the solution .
参考文献
| [1] | 李国栋.氧化物超细粉团聚机理研究[J].硅酸盐学报,2002(05):645-648. |
| [2] | 程海斌,刘桂珍,李立春,官建国,袁润章.纳米Fe3O4的ζ电位和分散稳定性[J].武汉理工大学学报,2003(05):4-6,26. |
| [3] | Wang J;Zhang K;Peng Z M .Magnetic properties improvement in Fe3O4 nanoparticles[J].Journal of Crystal Growth,2004,266:500. |
| [4] | Zhen S L.The factors on surface modification of powders[J].Journal of Chinese Nonmetal Industry,2003(01):13. |
| [5] | 赵慧君,张中杰,王德平,黄文旵,张娟.硅烷偶联剂对磁性纳米微球的磁性能影响[J].功能材料,2004(02):157-158,163. |
| [6] | Shi W X;Yang J;Wang T J .Surface organic modification of magnetic iron oxide black particles[J].Acta Physico-Chimica Sinica,2003,31(07):37. |
| [7] | 吴崇浩,王世敏.纳米微粒表面修饰的研究进展[J].化工新型材料,2002(07):1-5. |
| [8] | 汪汉斌,刘祖黎,卢强华,彭丽,姚凯伦.柠檬酸根对纳米Fe3O4颗粒的生长及性能的影响[J].无机化学学报,2004(11):1279-1283. |
| [9] | 江万权,朱春玲,朱玉瑞,陈祖耀,张培强.磁性粒子浓悬浮体系沉降稳定性的光学表征[J].化学物理学报,2001(05):601-605. |
| [10] | Xu XQ.;Shen H.;Xu JR.;Li XJ. .Aqueous-based magnetite magnetic fluids stabilized by surface small micelles of oleolysarcosine[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2004(1/4):430-436. |
| [11] | Huang Z B;Tang F Q .structure,and magnetic properties[J].Journal of Colloid and Interface Science,2004,275:142. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%